Abstract:Segmented carbon nanofibers were prepared by pyrolysis of acetylene on foam Ni at 600 and 700degreesC in a fixed bed flowed-reactor. The morphology, microstructure and lithium insertion properties of these carbon nanofibers were investigated by TEM, XRD, Raman and electrochemical methods. Through TEM observations, it was found that this kind of carbon nanofibers was composed of lens-like segments with nearly equal separation stacking along the nanofiber axis. When the reaction temperature was 600degreesC, segmented carbon nanofibers were the major production. However, when the reaction temperature increased to 700degreesC, the content of segmented carbon filaments decreased and their diameter became smaller. The crystallite size d(002) and L-c were determined by the 002 carbon Bragg peak of XRD patterns using the Bragg and Scherrer formulas. The intensity ratios of the 1350 cm(-1) line and the 1580 cm(-1) line (R =I-D/I-G) was used to evaluate the L-a value, which was inversely proportional to the effective crystallite size in the direction of the graphite plane (L-a). With the reaction temperature increased, the d(002) value decreased, L-a and L-c values increased, which indicated the degree of crystallinity increased. Segmented carbon nanofibers were used as positive electrodes of C/Li cells. The first charge capacities of C/Li cells were 480 and 300 mAh/g for samples produced at 600 and 700degreesC, respectively. The samples at 600degreesC showed capacities higher than the theoretical value of graphite, which was attributed to accommodation of more. lithium at the edge of graphene layers and on the surface of graphene layers according to the mechanisms of lithium insertion in carbons prepared by low-temperature pyrolysis of hydrocarbons. As confirmed by the XRD and Raman spectra, the samples at 700degreesC had larger L-a and L-c, which led to the capacity decreasing.

Preparation and Lithium Insertion Performance of Mesocarbon Microbeads

CHARGE DISCHARGE PROPERTIES OF THE MESOCARBON MICROBEADS FOR THE ANODS OF LITHIUM ION BATTERIES

An innovative and efficient method for the preparation of mesocarbon microbeads and their use in the electrodes of lithium ion batteries and electric double layer capacitors

Preparation of mesoporous carbon and its effect on properties of lithium-sulfur batteries

Wet-chemical Synthesized MCMB@Si@C Microspheres for High-Performance Lithium-Ion Battery Anodes.

Preparation and Characterization of Mesocarbon Microbeads by the Co-Polycondensation of High-Temperature Coal Tar Pitch and Coal Pyrolytic Extracts

Electrochemical Lithium Insertion Properties of Carbon Nanotubes Produced by Catalytic Pyrolysis of Acetylene

In Situ Nitrogen-Doped Helical Mesoporous Carbonaceous Nanotubes for Superior-High Lithium Anodic Performance

The charge-discharge properties of carbon materials prepared from coal for the anode of lithium ion batteries

CHARGE-DISCHARGE PROPERTIES OF MCMBs HEAT-TREATED WITH DIFFERENT TIME FOR THE ANODE OF LITHIUM ION BATTERIES

Improving the Performance of Biomass-Derived Carbons in Li-Ion Batteries by Controlling the Lithium Insertion Process

Controlled Synthesis of Ultrafine β-Mo2C Nanoparticles Encapsulated in N-Doped Porous Carbon for Boosting Lithium Storage Kinetics

Preparation of mesocarbon microbeads from coal tar pitch with blending of biomass tar pitch

A One-Step Hard-Templating Method for the Preparation of a Hierarchical Microporous-Mesoporous Carbon for Lithium-Sulfur Batteries

Synthesis and Characteristics of Nanoporous Carbon Spheres /S Composite as Cathode Material for Li-S Battery

Core‐Shelled MCMB‐Li4Ti5O12 Anode Material for Lithium‐ion Batteries

Lithium-Ion-Storage Behaviours of Cosb3 Intermetallic Compound and Effects of Some Carbonaceous Additives

Preparation and Electrochemical Lithium Intercalation Performance of Segmented Carbon Nanofibers

Introduction of as-prepared cobalt source-containing carbon nanotubes to Co1-S@C mesoporous nanospheres for an ultrahigh lithium storage

Controllable Morphologies and Electrochemical Properties of Graphitizing MCMB-based Hybrids with Nanostructure Via a Simple Chemical Vapor Deposition Method

Carbon Nanotube-Loaded Mesoporous LiFe0.6Mn0.4PO4/C Microspheres As High Performance Cathodes for Lithium-Ion Batteries