Abstract:This work investigated the effect of sintering temperatures (600–750°C) on mechanical and tribological behaviors of nickel-aluminium bronze (NAB) alloys developed by gas atomization and spark plasma sintering. Results indicated an increase of the volume fraction of B2-type NiAl precipitates with increasing sintering temperature, leading to an improvement of the yield strength and the wear resistance. Specifically, detailed microstructural analyses of sintered NAB alloys at 750°C showed the presence of ultrafine grains with an average size of 367nm, nanoscale twins with a volume fraction of 11.7% and dislocations with a density of 1.3 ± 0.1 × 1014m−2. A much higher yield strength of 620MPa was obtained in NAB, if compared to that of conventional cast counterparts (280–440MPa). Estimations of strengthening mechanisms suggested the predominant mechanism of grain boundary strengthening (335MPa) for NAB alloys with contributions from precipitate strengthening (54MPa), dislocation strengthening (75MPa), twin boundary strengthening (89MPa) and solid solution strengthening (50MPa). Moreover, dislocations was blocked at twin boundaries to form complex dislocation barriers and networks, further contributing to the high strength. The high wear resistance of NAB could be ascribed to the reduction of the local stress around crack tips due to the high elastic modulus mismatch (ENiAl/ECu), and to the crack extension toughening near the interface of the matrix and the precipitate caused by the high plastic mismatch (σNiAl/σCu).

Cavitation Erosion Behavior of Nickel-Aluminum Bronze Weldment

Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy

Cavitation erosion and corrosion behavior of copper–manganese–aluminum alloy weldment

The Synergistic Effect of Cavitation Erosion and Corrosion of Nickel-Aluminum Copper Surface Layer on Nickel-Aluminum Bronze Alloy

Correlation between microstructure and corrosion and cavitation erosion behaviors of nickel aluminum bronze

Why does seawater corrosion significantly inhibit the cavitation erosion damage of nickel-aluminum bronze?

Corrosion Mechanisms of Plasma Welded Nickel Aluminium Bronze Immersed in Seawater

Evolution Of The Corrosion Product Film On Nickel-Aluminum Bronze And Its Corrosion Behavior In 3.5 Wt % Nacl Solution

Erosion-corrosion behavior of Ni-Al-Cu coating on nickel-aluminium bronze alloy in 3.5 wt.% NaCl solution

Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions

Natural Seawater Impact on Crack Propagation and Fatigue Behavior of Welded Nickel Aluminum Bronze

Effects of Microstructure on the Stress Corrosion Cracking Behavior of Nickel-Aluminum Bronze Alloy in 3.5% NaCl Solution

Synergistic Effect Between Cavitation Erosion and Corrosion for Friction Stir Processed NiAl Bronze in Artificial Seawater

Recent Advances Of Nickel-Aluminum Bronze (Nab)

Cavitation erosion of the AA7050 aluminum alloy in 3.5 wt% NaCl solution—Part 1: mitigating effect by corrosion

Effect of Laser Surface Melting on Microstructure Evolution and Cavitation Behavior of Nickel Aluminum Bronze

Microstructure Design to Improve the Corrosion and Cavitation Corrosion Resistance of a Nickel-Aluminum Bronze

Cavitation-Erosion behavior of laser cladded Low-Carbon Cobalt-Based alloys on 17-4PH stainless steel

High Corrosion Resistance Nickel-Aluminum Bronze Prepared by Additive Manufacturing Followed by Laser Treatment

Cavitation erosion behavior of GH 4738 nickel-based superalloy

Microstructure, Mechanical and Tribological Properties of Nickel-Aluminium Bronze Alloys Developed Via Gas-Atomization and Spark Plasma Sintering