Abstract:Hypereutectic Al-Si alloys are used as material for the engine block and cylinder liners in automobiles. Wear behaviour of hypereutectic Al-Si alloy system changes significantly with applied normal load in both mild wear and severe wear regime. Significant improvement in wear resistance can be obtained by exposing silicon particles through the chemical etching process. For Al-25% Si alloys, most studies are reported in mild and ultra-mild wear regime. In the present work, the wear of exposed silicon particles with varying load and speed in severe wear regime was investigated under the unidirectional sliding condition and bi-directional sliding condition using a pin-on-disk tribometer (POD) and a linear reciprocating tribometer (LRT), respectively. Rapidly solidified and T6 heat-treated Al-25Si alloy was polished and etched using 5% NaOH solution to expose the silicon particles. Experiments were carried out with normal loads varying from 40 N to 120 N in dry sliding conditions. Sliding speeds of 0.8 m/s and 1.5 m/s were applied for each load in case of a pin on disk tribometer whereas, in an LRT, the sliding velocities were 0.2 m/s and 0.45 m/s respectively for each set of the load. The surface topography was measured by means of a 3-D optical profilometer, and surface morphology was analyzed using SEM images. It was observed that at higher loads, larger Si particles were fractured and pushed into the matrix. Fractured silicon particles, along with smaller particles, were embedded into the matrix, thereby increasing the silicon concentration in the wear region. The comparison of the experimental results of unidirectional and bi-directional sliding that reveal the change in surface morphology of silicon particles, the friction characteristics at the interface, variation of surface 3-D roughness parameters, the wear rate and wear mechanisms of Al-25% Si alloys are analyzed and reported in the study.

Microstructure of worn surface and wear debris of as-cast Al-17Si-xLa alloys under unlubricated conditions

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Dry sliding wear behavior of additively manufactured CoCrWNixAly alloys

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Dry sliding wear of MA/PM Al-10Ti alloy

Microstructural feature dependence of dry sliding wear behaviors in a γ-TiAl alloy

Dry sliding wear of microalloyed Er-containing Al–10Sn–4Si–1Cu alloy

A Comparison of the Sliding Wear Behavior of a Hypereutectic Al–Si Alloy Prepared by Spray-Deposition and Conventional Casting Methods

Effect of Heat Treatment on Tribological Properties of SiCp/Al–Mg–Mn–Cu Aluminum Matrix Composites

Tribological behavior of an AlCoCrFeNi2.1 eutectic high entropy alloy sliding against different counterfaces

Wear Behavior of a Heat-Treatable Al-3.5Cu-1.5Mg-1Si Alloy Manufactured by Selective Laser Melting

Sliding Friction and Wear Properties of GCr15 Steel under Different Lubrication Conditions

Microstructure and tribological behavior of a peak aged Cu–Cr–Zr alloy

Wear-resistance mechanism of an Al–12Si alloy reinforced with aluminosilicate short fibers

Tribological Behaviour of Al18B4O33-whisker-reinforced Hypoeutectic Al–Si–Mg-matrix Composites under Dry Sliding Conditions

Tribological Investigation of La2O3 Dispersed W-Ni-Cu Heavy Alloy Processed through Powder Metallurgy Process

Wear Properties of NiAl Based Materials

Wear and surface degradation of commercial ZTA femoral heads under boundary lubrication conditions

Tribological behaviour of hypereutectic Al-Si automotive cylinder liner material under dry sliding wear condition in severe wear regime

Study on Microstructure, Mechanical Properties and Erosion Characteristics of Al-Si Alloy Manufactured by Continuous Casting Direct Rolling Process

Friction and wear behavior of Fe2AlB2 nanolaminates against GCr15 steel counterpart