Influence of Mg content on ageing precipitation behavior of Al-Cu-Li-x alloys
Xiao-Ming Wang,Guo-Ai Li,Jian-Tang Jiang,Wen-Zhu Shao,Liang Zhen
DOI: https://doi.org/10.1016/j.msea.2018.11.015
2019-01-01
Abstract:The addition of minor Mg (~0.4 wt%) to Al-Cu-Li alloy could not only modify the precipitation path but also promote the precipitation of T1 (Al2CuLi) phase, however, the influence of higher Mg addition on the microstructures during ageing is still not clear. In this work, the influence of high Mg addition (>0.4 wt%) on the precipitation sequence, precipitation kinetics and the corresponding strengthening of an Al-Cu-Li alloy has been investigated by atom probe tomography (APT), transmission electron microscopy (TEM), differential scanning calorimetry (DSC) and tensile testing. For an Al-Cu-Li-0.4 wt% Mg alloy in the peak-aged condition, the microstructure contains a high density of fine T1 precipitates along with some non-negligible θ' phase (Al2Cu). When adding larger amount of Mg (0.8 wt%) to the alloy, however, the precipitation of S′ phase (Al2CuMg) is strongly accelerated at the expense of T1 and θ' phases. Much more Mg clusters are observed by APT at the early ageing stages of the high Mg-containing alloy, leading to more rapid hardening response. The precipitation kinetics for T1 phase become somewhat sluggish due to decreased nucleation sites and shortage of available solutes caused by formation of more S′ precipitates. The precipitation of coarse T1 and S′ phases is significantly detrimental to the ductility and toughness in the peak-aged condition for the high Mg-containing alloy.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering