Enhancing anti-wear and anti-corrosion performance of cold spraying aluminum coating by high current pulsed electron beam irradiation
Feng Guo,Wei Jiang,Guangze Tang,Zhiwen Xie,Hongbin Dai,Enhao Wang,Yongjun Chen,Lijun Liu
DOI: https://doi.org/10.1016/j.vacuum.2020.109772
IF: 4
2020-12-01
Vacuum
Abstract:<p>High current pulsed electron beam (HCPEB) was employed to irradiate cold spraying aluminum coating. The microstructures, tribological and corrosion behaviors of the untreated and irradiated samples were investigated by the X-ray diffraction (XRD), scanning electron microscope (SEM), ball-disc wear and electrochemical tests. HCPEB irradiation significantly triggered the surface remelting and densification of the coating texture. Compared with the original coating, the irradiated coating showed a higher hardness of up to 88 HV, a higher compressive stress value of 31 MPa and a lower wear rate of 1.06 × 10<sup>−4</sup> mm<sup>3</sup> N<sup>−1</sup> m<sup>−1</sup>, but also exhibited an outstanding anti-corrosion performance, reflected by a higher polarization resistance and a smaller corrosion current density of 4.45 μA/cm<sup>2</sup>. These current findings confirmed that HCPEB irradiation shows a huge potential for enhancing the anti-corrosion and anti-wear properties of cold spray coatings.</p>
materials science, multidisciplinary,physics, applied