Enhancing Corrosion Resistance of AISI 316L Steel Surface Alloyed with Ti by High Current Pulsed Electron Beam

ZHANG Ke-min,ZOU Jian-xin,YANG Da-zhi

DOI: https://doi.org/10.3969/j.issn.1009-6264.2006.05.026

2006-01-01

Abstract:The rapid surface alloying of AISI 316L stainless steel by high current pulsed electron beam(HCPEB) was investigated.A fine Ti powder layer was pre-coated on the substrate and then post-treated with HCPEB.Due to the rapid surface heating,melting,mixing and enhanced diffusion effects,part of the Ti coating was dissolved into the substrate,forming a Ti-rich layer on the top surface.Since the addition of Ti favors the formation of α phase,the alloyed layer contains a mixture of α and γ phases.Potentiodynamic tests in the simulated body fluid show that the corrosion resistance of AISI 316L stainless steel can be effectively improved after HCPEB surface alloying with Ti.