Wear Resistance of In-situ Austenite Steel Matrix Composites Reinforced with Granular Eutectics

梁高飞,许振明,姜启川,李建国

DOI: https://doi.org/10.3321/j.issn:1004-0595.2003.02.008

2003-01-01

Abstract:Austenite matrix composites reinforced with granular γ-(Fe, Mn)3C binary eutectics (EAMC) were prepared by means of the non-oxidation melting in a medium frequency induction oven. The wear resistance of the resulting composites in dry sliding against AISI1045 steel was examined on a pin-on-disc test rig. The structure of the composites was observed with an optical microscope, while the worn surface morphologies were observed with a scanning electron microscope. As a result, three regimes including the mild wear regime, the transition regime from slight wear to serious wear, and the serious wear regime were identified for the composites, by taking into account the relationship between the wear rate and the applied load. The composites were characterized by abrasive wear in the mild wear regime and the transition regime, and by oxidation wear in the severe wear regime. The better wear resistance of the composites than that of the austenite medium Mn steel at low and medium loads was attributed to the strengthening function of γ-(Fe, Mn)3C binary eutectics. At higher loads, the flake-shaped granular eutectic embedded into the austenite matrix led to severe oxidation wear and hence increased the wear rate of EAMC. The composites experienced a transition to the severe wear regime at a higher load as compared with the matrix alloy, owing to their better thermal dissipation ability and strength-retaining ability at elevated temperature in the presence of the granular eutectic particles. The chemical composition of the austenite steel which is used as the matrix of the composite material is C-Mn-Si-P-S-O.