Fatigue failure analysis and life prediction of wheel load local area of ladle crane
Guoqian Wei,Qingzheng Yin,You Zhao,Zhang Dang,ZHIWEN LU
DOI: https://doi.org/10.1088/1361-6501/ad7751
IF: 2.398
2024-09-05
Measurement Science and Technology
Abstract:Metal structures of ladle cranes are typical complex welded structures,where fatigue cracks are prone to initiate in some specific locations.In this paper,on-site tests and theoretical analysis were performed for a in-service ladle crane to investigate the crack damage mechanism at some local areas beneath the wheel loads. The on-site tests included crack observation of the entire bridge structure, geometry inspection of the main girder and stress test of the key locations. It was found that fatigue cracks had densely occurred in some spots with similar geometry details. The stress test results showed that obvious rail gnawing phenomenon happened during the ladle crane operating process. By finite element analysis (FEA) with a multi-layer model and DLOAD subroutine, stress time histories of the damaged spots under moving wheel loads were simulated. Combined with the tested stresses, influences of rail gnawing force on the stress cycling characteristics at the cracked areas were analyzed. Based on the in-service stress spectrum, the fatigue lives of the cracked areas were predicted, revealing that the random rail gnawing force is the dominant factor causing large amount of cracks at the damaged areas.
engineering, multidisciplinary,instruments & instrumentation