Abstract:Layered borosilicate zeolite precursor ERB-1P (Si/B = 11) is delaminated via simultaneous deboronation and SDA removal, to yield material DZ-1 consisting of silanol nests, using a simple aqueous Zn(NO3)2 treatment. Characterization of this synthesis process by PXRD shows loss of long-range order, and transmission electron microscopy (TEM) demonstrates transformation of rectilinear layers in the layered zeolite precursor to single and curved layers in the delaminated material. N2 physisorption confirms the expected decrease of micropore volume and increase in external surface area for delaminated materials relative to their calcined 3D zeolite counterpart. Elemental analysis shows loss of B and absence of Zn in the delaminated material. Resonances corresponding to silanol nests are evident via (29)Si solid-state NMR spectroscopy in DZ-1, which should be located within 12-MR pockets near the external surface. We have successfully utilized these nests as tetrahedral recognition sites for incorporation of Ti within an isolated framework coordination environment in material Ti-DZ-1. Diffuse-reflectance ultraviolet (DR-UV) spectroscopy of Ti-DZ-1 confirms isolated framework Ti sites, which are assigned to bands in the range of 210 nm-230 nm. Infrared spectra of Ti-DZ-1 consist of a distinct absorption band at 960 cm(-1), which is absent in DZ-1 prior to Ti incorporation and has been previously correlated with the presence of framework Ti species. Infrared spectra after pyridine adsorption demonstrate bands consistent with Lewis-acid sites in the resulting Ti-substituted delaminated zeolite. The accessibility of these Lewis-acid sites is confirmed when using Ti-DZ-1 as a catalyst for cyclohexene epoxidation using tert-butyl hydroperoxide as the organic oxidant - a reaction for which both DZ-1 and TS-1 are inactive.

Preparation and characterization of a novel amphiphilic Ti-β zeolite

Preparation of amphiphilic TS-1 zeolites and their phase-boundary catalysis

A novel liquid-solid isomorphous substitution route for preparing zeolite Ti-beta

Preparation of Amphiphilic Zeolites with Various Pore Structure and Their Catalytic Performance for Phase-Boundary Reaction

High Load Rare-earth β Zeolite Prepared by Solid Medium-In-Situ Synthesis Method and Its Catalytic Cracking Performance

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

Preparation and Characterization of Amphiphilic HZSM-5 Zeolite with Various Si/Al Ratios

Tailoring Porosity and Titanium Species of TS-1 Zeolites via Organic Base-assisted Sequential Post-treatment

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Preparation and Catalytic Performance in Propylene Epoxidation of Hydrophobic Hierarchical Porous TS-1 Zeolite

Synthesis and characterization of β zeolite from aluminosilicate sol containing fluorion

Tailoring the structure of hierarchically porous zeolite beta through modified orientated attachment growth in a dry gel system.

Highly Hydrophilic Ti−Beta Zeolite with Ti−Rich Exterior as Efficient Catalyst for Cyclohexene Epoxidation

Preparation of titanium-containing zeolites with MEL structure from B-ZSM-11 and their characterization

Characterization of Titanium-Modified USY Zeolites and Their Catalytic Performance on N-Heptane Cracking

Novel Surfactant-Free Route to Delaminated All-Silica and Titanosilicate Zeolites Derived from a Layered Borosilicate MWW Precursor

Preparation and Structural Characterization on Organic-inorganic Hybrid Acid-base Bifunctional High Silica Y Zeolite

Synthesis of small crystal zeolite beta in a biphasic H2O–CTAB–alcohol system

Preparation and Catalytic Performance of Noble Metal Loaded Core-Shell Structured Catalyst

Preparation and Characterization of Titanium-Containing MFI from Highly Siliceous ZSM-5: Effect of Precursors Synthesized with Different Templates