Abstract:Purposive regulation of the spatial location and distribution of acid sites in a zeolite catalyst, though still rather challenging, has proved to be an effective measure to enhance its performance in the conversion of methanol to olefins (MTO). Herein, a series of ZSM-11 zeolites were synthesized using different sodium halides (with tetrabutylammonium hydroxide (TBAOH) as the structure-directing agent); the effect of halogen anions (Cl-, Br- and I-) in the synthesis gel on the Al siting and thereon the spatial location and distribution of acid sites in the ZSM-11 zeolites as well as their relation to the catalytic performance in MTO was elaborately investigated. The results indicate that for the synthesis of high Si/Al ratio ZSM-11 zeolites (Si/Al > 60), the Cl- anions present in the synthesis gel can induce more Al atoms siting on the external surface of ZSM-11 crystals, thereby leading to a short catalytic lifetime in MTO due to the rapid coke deposition. In contrast, larger Br- or I- anions in the synthesis gel, owing to their stronger covalent interaction with the TBA+ cations, may moderate the formation of crystal silicate nuclei and lead to a uniform distribution of Al species in the inner straight channels, which can effectively suppress the surface coke deposition and inhibit the aromatic-based cycle for MTO. As a result, the high Si/Al ratio ZSM-11 zeolites obtained with Br- or I- in the synthesis gel exhibit much better catalytic stability in MTO and higher selectivity to propene and butene, in comparison with the ZSM-11 counterpart synthesized using Cl-. These results help to clarify the relation between the catalytic performance of ZSM-11 in MTO and the location of acid sites and thus bring forward a facile strategy to enhance the catalytic performance of zeolites through purposively regulating the spatial distribution of acid sites.

Preparation of titanium-containing zeolites with MEL structure from B-ZSM-11 and their characterization

Preparation and Characterization of Titanium-Containing MFI from Highly Siliceous ZSM-5: Effect of Precursors Synthesized with Different Templates

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

Preparation and catalytic performance of the supported Ti-MWW zeolites

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

NMR Study on the Acidity of TS-1 Zeolite

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Preparation and characterization of a novel amphiphilic Ti-β zeolite

Structures of highly siliceous ZSM-5 zeolites and Ti- ZSM-5 zeolites obtained by indirect synthesis

Preparation and Catalytic Performance of Noble Metal Loaded Core-Shell Structured Catalyst

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Structure of Highly Siliceous ZSM-5 Zeolites and Ti-ZSM-5 Zeolites Obtained by Indirect Synthesis

Synthesis and Investigation of Zeolite TiO2/Al-ZSM-12 Structure and Properties

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

Preparation of Amphiphilic Zeolites with Various Pore Structure and Their Catalytic Performance for Phase-Boundary Reaction

Novel Surfactant-Free Route to Delaminated All-Silica and Titanosilicate Zeolites Derived from a Layered Borosilicate MWW Precursor

Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media

Regulating the distribution of acid sites in ZSM-11 zeolite with different halogen anions to enhance its catalytic performance in the conversion of methanol to olefins

Insight into the formation of framework titanium species during acid treatment of MWW-type titanosilicate and the effect of framework titanium state on olefin epoxidation

Deboronation-assisted Construction of Defective Ti(OSi)3OH Species in MWW-type Titanosilicate and Their Enhanced Catalytic Performance

Tailoring Porosity and Titanium Species of TS-1 Zeolites via Organic Base-assisted Sequential Post-treatment