Abstract:In this study of the synthesis of SAPO-34 molecular sieves, XRD, SEM, XRF, IR and NMR techniques were applied to monitor the crystalloid, structure and composition changes of the samples in the whole crystallization process in order to get evidence for the crystallization as well as Si incorporation mechanism of SAPO-34. XRD results revealed that the crystallization contained two stages. In the first 2.5 h (the earlier stage), high up to ∼80% of relative crystallinity could be achieved and the crystal size of SAPO-34 was almost the same as that of any longer time, indicating a fast crystallization feature of the synthesis. In this stage, IR revealed that the formation of SAPO-34 framework structure was accompanied by the diminution of hydroxyls, suggesting that crystal nuclei of SAPO-34 may arise from the structure rearrangement of the initial gel and the condensation of the hydroxyls. NMR results reveal that the template and the ageing period are crucial for the later crystallization of SAPO-34. Preliminary structure units similar to the framework of SAPO-34 have already formed before the crystallization began (0 h and low temperature). Evidence from IR, NMR, and XRF shows that the formation of the SAPO-34 may be a type of gel conversion mechanism, the solution support and the appropriate solution circumstance are two important parameters of the crystallization of SAPO-34. Meanwhile, NMR measurements demonstrated that about 80% of total Si atoms directly take part in the formation of the crystal nuclei as well as in the growth of the crystal grains in the earlier stage (<2.5 h). Evidence tends to support that Si incorporation is by direct participation mechanism rather than by the Si substitution mechanism for P in this stage (<2.5 h). In the later stage (>2.5 h), the relative content of Si increased slightly with a little decrease of Al and P. The increase of Si(4Al) and the appearance of the Si(3Al), Si(2Al), Si(1Al) and Si(0Al) in this stage suggest that substitution of the Si atoms for the phosphorus and for the phosphorus and aluminum pair takes place in the crystallization. The relationship among structure, acidity and crystallization process is established, which suggests a possibility to improve the acidity and catalytic properties by choosing a optimum crystallization time, thus controlling the number and distribution of Si in the framework of SAPO-34.

Crystallization Process of Sapo-34 Molecular Sieve Using Hydrogen Fluoride and Triethylamine As Composite Template

Synthesis of Sapo-34 Molecular Sieve Using Hydrogen Fluoride and Triethylamine As Composite Template

Study on the crystallization mechanism of molecular sieve SAPO-34

Crystallization and Si incorporation mechanisms of SAPO-34

Synthesis of SAPO-34 Molecular Sieve by Liquid-Phase Crystallization

Synthesis of SAPO-34 Molecular Sieves and Their Catalytic Performances in Methanol-to-Olefins Reaction

Study on Synthesis of Sapo-34 Molecular Sieve Using Composite Template Teaoh-Morpholine Ii. Surface Acidity and Catalytic Performance of Sapo-34 Molecular Sieve

Preparation of Fe@Si/S-34 Catalysts and Its Catalytic Performance for Syngas to Olefins

Effect of kaolin calcined temperature on the preparation and crystallization mechanism of SAPO-34 molecular sieve for methanol-to-olefins performance

METHOD AND MECHANISM OF Si INCORPORATION INTO LATTICE OF SAPO-34 MOLECULAR SIEVE

Synthesis and Crystallization Mechanism for SAPO‐34 Zeolite Derived from Magadiite

Preparation of floral mesoporous SAPO-34 with the aid of fluoride ion

Synthesis of SAPO-34 with the Presence of Additives and Their Catalytic Performance in the Transformation of Chloromethane to Olefins

Effect of silica/alumina ratio and structure-directing agent on the physical and chemical properties of SAPO-34

Synthesis of SAPO-34 catalyst with different silicon contents and their catalytic performance in chloromethane to olefins

Direct evidence of time-dependent crystallization evolution of SAPO-34 and SAPO-20 zeolites directed by trimethylbenzylammonium hydroxide for microwave-assisted ethanolysis of furfuryl alcohol

Unraveling the non-classic crystallization of SAPO-34 in a dry gel system towards controlling meso-structure with the assistance of growth inhibitor: Growth mechanism, hierarchical structure control and catalytic properties

In-Situ Synthesis of Sapo-34 Molecular Sieves on Monolithic Cordierite Substrates

Synthesis, characterization and catalytic performance of SAPO-34 molecular sieves for methanol-to-olefin (MTO) reaction

Catalytic and deactivated behavior of SAPO-34/ZSM-5 composite molecular sieve synthesized by in-situ two-step method

Phase-transformation synthesis of SAPO-34 and a novel SAPO molecular sieve with RHO framework type from a SAPO-5 precursor