Abstract:In this study of the synthesis of SAPO-34 molecular sieves, XRD, SEM, XRF, IR and NMR techniques were applied to monitor the crystalloid, structure and composition changes of the samples in the whole crystallization process in order to get evidence for the crystallization as well as Si incorporation mechanism of SAPO-34. XRD results revealed that the crystallization contained two stages. In the first 2.5 h (the earlier stage), high up to ∼80% of relative crystallinity could be achieved and the crystal size of SAPO-34 was almost the same as that of any longer time, indicating a fast crystallization feature of the synthesis. In this stage, IR revealed that the formation of SAPO-34 framework structure was accompanied by the diminution of hydroxyls, suggesting that crystal nuclei of SAPO-34 may arise from the structure rearrangement of the initial gel and the condensation of the hydroxyls. NMR results reveal that the template and the ageing period are crucial for the later crystallization of SAPO-34. Preliminary structure units similar to the framework of SAPO-34 have already formed before the crystallization began (0 h and low temperature). Evidence from IR, NMR, and XRF shows that the formation of the SAPO-34 may be a type of gel conversion mechanism, the solution support and the appropriate solution circumstance are two important parameters of the crystallization of SAPO-34. Meanwhile, NMR measurements demonstrated that about 80% of total Si atoms directly take part in the formation of the crystal nuclei as well as in the growth of the crystal grains in the earlier stage (<2.5 h). Evidence tends to support that Si incorporation is by direct participation mechanism rather than by the Si substitution mechanism for P in this stage (<2.5 h). In the later stage (>2.5 h), the relative content of Si increased slightly with a little decrease of Al and P. The increase of Si(4Al) and the appearance of the Si(3Al), Si(2Al), Si(1Al) and Si(0Al) in this stage suggest that substitution of the Si atoms for the phosphorus and for the phosphorus and aluminum pair takes place in the crystallization. The relationship among structure, acidity and crystallization process is established, which suggests a possibility to improve the acidity and catalytic properties by choosing a optimum crystallization time, thus controlling the number and distribution of Si in the framework of SAPO-34.

Unraveling the non-classic crystallization of SAPO-34 in a dry gel system towards controlling meso-structure with the assistance of growth inhibitor: Growth mechanism, hierarchical structure control and catalytic properties

Ingrown Leading to Hierarchical SAPO‐34 with High Catalytic Activity

Controlled synthesis of high performance SAPO-34 with sheet-like morphology and small particle size using concentrated gel system

Crystallization and Si incorporation mechanisms of SAPO-34

Nonclassical from-shell-to-core growth of hierarchically organized SAPO-11 with enhanced catalytic performance in hydroisomerization of n-heptane

Synergic regulation of crystalline phase, composition and morphology of SAPO-34 via metal assistance and in situ etching strategy

Generating Nanocrystalline SAPO-34 Through Bead-Milling and Porogen-Assisted Recrystallization: Structural Evolution and Catalytic Consequence in Dimethyl Ether-to-olefin Conversion

Interface Mediated Crystallization of Plate-Like SAPO-41 Crystals to Promote Catalytic Hydroisomerization

Changing Template/Al2O3 Ratio in Reaction Gel—An Effective Way to Regulate Nature of Intermediate Phases and Properties of SAPO-11 Molecular Sieves during Crystallization

Study on the crystallization mechanism of molecular sieve SAPO-34

Self-assembly of silicoaluminophosphate nanocrystals in biphasic media with a water-insoluble structure-directing agent

Hierarchical Silicoaluminophosphate Catalysts with Enhanced Hydroisomerization Selectivity by Directing the Orientated Assembly of Premanufactured Building Blocks

Synthesis and Crystallization Mechanism for SAPO‐34 Zeolite Derived from Magadiite

Crystallization of SAPO-11 Molecular Sieves Prepared from Silicoaluminophosphate Gels Using Boehmites with Different Properties

Crystallization Process of Sapo-34 Molecular Sieve Using Hydrogen Fluoride and Triethylamine As Composite Template

Manipulating the Mesostructure of Silicoaluminophosphate SAPO-11 Via Tumbling-Assisted, Oriented Assembly Crystallization: a Pathway to Enhance Selectivity in Hydroisomerization

Conquering the Solubility Barrier of Di-N-octylamine As Structure-Directing Agent in Hierarchical Silicoaluminophosphate Synthesis by Using Phase-Transfer Synthesis

Synthesis of SAPO-34 nanocrystallites by epoxy-functional organosilane with improved MTO catalytic performance

Crystal Engineering of Hierarchical Zeolite in Dynamically Maintained Pickering Emulsion

Synthesis and Catalytic Performances of Hierarchical Sapo-34 Monolith

Controlled synthesis of hierarchically porous SAPO-34 zeolites with tailored crystal size and morphology