Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Effect of TiO2 surface properties on the SCR activity of NOx emission abatement catalyst.

Insights into the Effects of Sulfate Species on CuO/TiO2 Catalysts for NH3-SCR Reactions

Influence of texture structures of TiO2 supports on surface properties and SCR performance of V2 O5-MoO3/TiO2 catalyst

Effect of Dispersion State and Surface Properties of Supported Vanadia on the Activity of V2O5/TiO2 Catalysts for the Selective Catalytic Reduction of NO by NH3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Investigations of Surface VOx Species and Their Contributions to Activities of VOx/Ti0.5Sn0.5O2 Catalysts Toward Selective Catalytic Reduction of NO by NH3

Exploring the Role of V2O5 in the Reactivity of NH4HSO4 with NO on V2O5/TiO2 SCR Catalysts

Revealing the Correlation Between Surface Acid Sites and Activity of VPO/TiO2 Catalyst

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Ti3+ doped V2O5/TiO2 catalyst for efficient selective catalytic reduction of NOx with NH3

Nh3 Selective Catalytic Reduction of No: A Large Surface Tio2 Support and Its Promotion of V2o5 Dispersion on the Prepared Catalyst

Promotion effect of Ce and Ta co-doping on the NH3-SCR performance over V2O5/TiO2 catalyst

Interface sites on vanadia-based catalysts are highly active for NOx removal under realistic conditions

Promotion Effect of Tungsten Oxide on SCR of NO with NH3 for the V2O5–WO3/Ti0.5Sn0.5O2 Catalyst: Experiments Combined with DFT Calculations

The Properties and SCR De‐nox Application of Supported V2O5/TiO2 Catalysts with Different Polymerization State of VOx Species Controlled by the Ph Value of Their Precursors

One-step Synthesized SO42--TiO2with Exposed(001)facets and Its Application in Selective Catalytic Reduction of NO by NH3

One-step synthesized SO42–-TiO2 with exposed (001) facets and its application in selective catalytic reduction of NO by NH3

TiO2-Supported Catalysts in Low-Temperature Selective Reduction of NOx with NH3: A Review of Recent Progress

Active sites of NO selective catalytic reduction over V2O5-WO3/TiO2