Structural Characterization and Magnetic Properties of Single‐crystalline (la0.6pr0.4)0.67ca0.33mno3 Nanowires
Weiren Xia,Kai Leng,Qingkai Tang,Li Yang,Yuting Xie,Zhiwei Wu,Kang Yi,Xinhua Zhu
DOI: https://doi.org/10.1111/jace.17773
IF: 4.186
2021-01-01
Journal of the American Ceramic Society
Abstract:Herein, structural and magnetic properties of single-crystalline (La0.6Pr0.4)(0.67)Ca0.33MnO3 nanowires synthesized via a hydrothermal process are reported. The nanowires are crystallized in an orthorhombic structure (Pnma space group). Their lattice parameters follow the relationship a approximate to c approximate to b/root 2. These nanowires exhibited a clean and smooth surface with diameters of 60-120 nm and an average length of approximately 2.0 mu m. High-resolution transmission electron microscopy images confirmed the single-crystalline nature of the nanowires growing along the [100] direction. The nanowires demonstrated magnetic hysteresis loops at low temperatures and a weak exchange bias (EB) effect. Paramagnetic (PM)-ferromagnetic (FM) phase transition occurred at a Curie temperature (T-C) of 224 K, and strong irreversibility between zero-field-cooled (ZFC) and field-cooled (FC) magnetization (M-ZFC and M-FC, respectively) curves was observed at 273 K. The M-ZFC curve exhibited a significantly broad peak with a maximum at a freezing temperature (T-f) of 134 K. Relative difference between M-FC and M-ZFC in the nanowires [(M-FC - M-ZFC)/M-FC] rapidly increased below T-f and reached approximately 50% below 35 K. The effective magnetic moment deduced from the Curie constant is larger than the theoretical value, indicating short-range FM interactions in the nanowires. A positive PM T-C (theta(p)) implies dominant FM interactions in the nanowires, and theta(p) > T-C observed herein indicates the existence of short-range ordered states above T-C.