Structure And Luminescence Properties Of Eu3+ Doped Sio2 Glass Synthesized By Sol-Gel Process
Xg Wang,Hy Wu,Dt Xie,Sf Weng,Jg Wu
IF: 4.632
2002-01-01
Journal of Rare Earths
Abstract:Under different annealing temperatures, Eu3+-doped SiO2 gel and glass were prepared by sol-gel method, and the structure and luminescent properties were studied with excitation spectra, emission spectra, IR and DTA-TG. The results show that the fluorescent intensity tends to get stable when concentration of Eu3+ doped is above 1.86 % (mass fraction) most water absorbed by the gel was removed at 300 degreesC, and that the emission spectrum of Eu3+, with peaks at 614, 588, 577 nm, is due to D-5(0)-->F-7(2), D-5(0)-->F-7(1), D-5(0)-->F-7(0) transitions, and the excitation peaks at 318, 362, 380, 393, 412 and 462 nm were observed. These results illustrate that the temperature range of 300 similar to 500 degreesC is critical for the structure conversion from gel to glass, and the fluorescence is strongly quenched by water.