Red photoluminescence from GeO2-SiO2 gel-glasses prepared by a new sol-gel process

Heqing Yang,Xuan Wang,BangLao Zhang,Yongfang Li,Liangying Zhang,Xi Yao

2002-01-01

Abstract:The GeO2-SiO2 gel-glasses were prepared by the sol-gel method with tetraethoxysilane (Si (OC2H5)4) and 3-trichlorogermanium propanoic aci (Cl3GeCH2CH2COOH) as starting materials. The gel-glasses show a strong room-temperature photoluminescence with peaks at 575 and 624 nm under the excitation of the 532 nm line of a Nd : YAG laser. The photoluminescence spectra are caused by GeO2 nanoparticles embedded in gel-glasses. The GeO2-SiO2 gel-glasses are characterized by the optical absorption, X-ray diffraction (XRD) and transmission election mecroscopy. The size of GeO2 nanoparticles embedded in gelglasses becomes larger as the GeO2 content increases, and thus the optical absorption edge of the gel-glass shifts to the lower-energy side. The GeO2 nanoparticle structures are found to be amorphous GeO2 in the gel-glasses by the XRD and the electron diffraction pattern.