Abstract:The present investigation was conducted on the low-speed impact response of quasi-isotropic [±45/0/90°]xs hybrid composite through laboratory level experimental tests. The purpose was to understand the behaviour that the different stacking sequences of hybrid glass/carbon fibre composites has on the ability of the material to sustain loads during low-speed impact events without developing critical structural failure in the material and improving the impact energy absorption properties, which is a relevant matter in aerospace and automotive industries. Drop-weight impact tests were carried out on two different laminates, with different stacking sequences, each of which were 16 symmetric inter-ply hybrid laminates named GC [+45G/−45C/0G/90C]4s and, respectively, G-C [+45G/−45G/0G/90G/+45C/−45C/0C/90C]2s, where G stands for glass fibre and C for carbon fibre. Both were comprised of epoxy matrix reinforced carbon/E-glass fibre woven fabric composites. The outcome of changing the hybrid stacking sequence, on the impact performances, was discussed. The damage morphologies and local failure mechanisms were analysed using visual inspection and a high-resolution laser scanner. Under 33 J impact energy, both tested hybrid composites exhibited approximately 10 kN peak load. Nevertheless, one key parameter, the time to peak load, significantly changed; the damage initiation threshold for GC samples occurred immediately before 6 kN, whereas for G-C samples this threshold appeared much earlier. This type of behaviour was partly connected to the delay in the propagation of delamination and fibre breakage, which was influenced by the high elastic energy absorption of the carbon fibres when compared with the glass fibres. The absorbed energy was higher for GC configuration, whereas a higher DI was observed for samples G-C indicating that a high percentage of the total energy was dissipated through the propagation of in-plane and out-of-plane fibre/matrix cracks. No perforation was observed on either configuration; nevertheless, the damage area significantly changed both in size and appearance from one configuration to another.

Effects of Geometric and Material Factors on Mechanical Response of Laminated Composites Due to Low Velocity Impact

Cross-helicoidal Approach to the Design of Damage-Resistant Composites

Finite element analysis on impact response and damage mechanism of composite laminates under single and repeated low-velocity impact

Analysis on the impact response of fiber-reinforced composite laminates: an emphasis on the FEM simulation

Failure Analysis of Carbon Fiber Reinforced Composite Subjected to Low Velocity Impact and Compression after Impact

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Low‐velocity impact behavior of composite laminates based on bio‐inspired stacking sequence

Experimental and numerical response and failure of laterally impacted carbon/glass fibre-reinforced hybrid composite laminates

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact

Low‐velocity impact damage and compression after impact behavior of CF/PEEK thermoplastic composite laminates

Research on low‐velocity impact resistance of carbon fiber composite laminates

An Efficient Numerical Method to Analyze Low‐velocity Impact Response of Carbon Fiber Reinforced Thermoplastic Laminates

Low Velocity Impact Response of Carbon Fiber Composite Laminates with Surface Glass Fibers

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Impact Behavior and Residual Strength of PEEK/CF-Laminated Composites with Various Stacking Sequences

Numerical modeling and experimental validation of low velocity impact of woven GFRP/CFRP composites

Low‐velocity multiple impact damage characteristics and numerical simulation of carbon fiber/epoxy composite laminates

Investigation on Layer Hybridization of Glass/Carbon Fibre Woven Reinforced Composites Subjected to Low-Speed Impact

Low velocity impact behavior and simulation of parametric effect analysis for UHMWPE/LLDPE thermoplastic composite laminates

Bridging the Effect of the Impactor Head Shape to the Induced Damage during Impact at Low Velocity for Composite Laminates

Compressive Failure of Carbon/Epoxy Laminate Composites under High Impact Loading