EFFECT MECHANISM OF Mn CONTENTS ON SHAPE MEMORY OF Fe-Mn-Si-Cr-Ni ALLOYS
Chengyan ZHANG,Fan SONG,Shanling WANG,Huabei PENG,Yuhua WEN
DOI: https://doi.org/10.11900/0412.1961.2014.00394
2023-01-01
Abstract:Fe-Mn-Si base shape memory alloys (SMAs), as compared with Ni-Ti and Cu base SMAs, have attracted much attention since the 1980s due to their promising advantages, such as low cost, good workability and weldability. However, the recovery strain of polycrystalline Fe-Mn-Si base SMAs is only about 2%-3% except single crystals and ribbons ones. At the present time, in order to enhance the recovery strain of this kind of alloys, some methods such as thermo-mechanical training, ausforming and thermo-mechanical treatment are used. In recent years, the research group had prepared training- free cast Fe- Mn- Si base alloys showing an excellent shape memory effect (SME). Unfortunately, the grains of cast Fe-Mn- Si base alloys are coarse, certainly leading to low yield strength and recovery stress. Many factors affecting the shape memory effect, such as alloy elements, the amount of pre-strain, deformation temperatures, annealing treatments and the training, have been studied. However, there is a debate on the effect of Mn contents on the shape memory effect of Fe-Mn-Si base alloys. The aim of this work is to clarify the debate, shape memory effect and microstructures of solution treated Fe-(14-21)Mn-5.5Si8.5Cr-5Ni alloys were investigated by OM, EBSD, XRD, TEM and SQUID before and after deformation at 10 K higher than their start temperature of martensitic transformation (M-5+10 K)..The result showed that the shape memory effect of solution treated Fe-(14 similar to 21)Mn-5.5Si-8.5Cr-5Ni alloys increased with the Mn contents. There are two reasons for this result. One is that the difference value between austenitic yield strength and critical stress of stressinduced E martensite increased with the Mn contents. In other word, the ability resisting plastic deformation was improved by increasing the Mn contents. The other is that the reversibility of epsilon martensite reverse transformation was enhanced by increasing the Mn contents because the width of stress-induced epsilon martensite decreased while the alpha' martensite was difficult to be introduced with increasing the Mn contents.