Abstract:Al-6.0Mg-0.3Sc alloy deposits are prepared by means of a double-wire arc additive manufacturing process. The formation, porosity, metallographic structure, type of precipitated phase, and mechanical properties of the deposit are studied. Double-wire arc forming affords precision advantages over single-wire-arc forming, which is evidenced by the increased surface uniformity of the deposit. Compared with the deposit of single-wire-arc formed, the deposit of double-wire arc formed exhibits only fewer and smaller pores, and the lower process heat yields rapid solidification and tiny precipitate sizes. A larger amount of Mg and Mn is observed to be dissolved in the Al matrix of double-wire arc-formed deposit, which increases the alloy strength, and smaller primary Al<sub>3</sub>Sc phase, which exhibits excellent grain refinement. Furthermore, the presence of a high amount of Sc solid solution in the matrix of double-wire arc-formed deposit strengthens the alloy, and the melting of the rear wire "heat-treats" the substrate formed by the front wire, promotes secondary Al<sub>3</sub>Sc phase precipitation, and further strengthens the alloy. Compared with the deposit of single-wire-arc formed, the mechanical properties of double-wire arc-formed deposit show an improvement: the tensile strength, yield strength, and elongation of the horizontally oriented specimens are estimated as 363 MPa, 258 MPa, and 26%, respectively. This successful implementation of the cold metal transfer + pulse process to prepare Al-Mg alloy parts can pave the way to their industrial production. The proposed method can find wide utility in the fields of aviation, aerospace, military, and shipbuilding.

Microstructure and Properties of AlSi17Fe6Cu4.5Mg0.5 Alloy Prepared by Rapid Solidification

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Microstructural evolution and mechanical properties of the rapidly-solidified and hot-extruded 2196 Al-Li alloy

Microstructure and mechanical properties of Al-Mg-Si alloy fabricated by a short process based on sub-rapid solidification

A Novel Method for Improving the Microstructure and Properties of Al-Si-Cu Alloys Based on Rapid Solidification/Powder Metallurgy

A novel method for improving the microstructure and the properties of Al-Si-Cu alloys prepared using rapid solidification/powder metallurgy

Thermal stability and its effects on the mechanical properties of rapidly solidified Al-Ti alloys

Mechanical properties of rapidly solidified Al-Ti alloys after thermal exposure

Microstructural evolution and mechanical properties of an ultrahigh-strength Al−Zn−Mg−Cu alloy via powder metallurgy and hot extrusion

Microstructure and Mechanical Properties of Al-Si Alloys Produced by Rapid Solidification and Hot Extrusion

The microstructures and properties of an al- 12 wt pct

Investigation of Microstructures and Mechanical Properties of Ultra-High Strength Al-Zn-Mg-Cu Alloy Prepared by Rapid Solidification and Hot Extrusion

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Formation of Spheroidal Microstructure in Semi-solid State of Al-4.8Si-2.8Cu-0.5Mg Aluminium Alloy

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting

Microstructure and Mechanical Properties of a Novel Al-Mg-Sc-Ti Alloy Fabricated by Laser Powder Bed Fusion

Effect of the Addition of Cu and Al on the Microstructure, Phase Composition and Properties of a Ti-6Al-4V Alloy Obtained by Selective Laser Melting

Heterogeneous microstructure and mechanical behaviour of Al-8.3Fe-1.3V-1.8Si alloy produced by laser powder bed fusion

Microstructure and Properties of Al-6.0Mg-0.3Sc Alloy Deposited by Double-Wire Arc Additive Manufacturing

Correlation of Solidification Microstructure Refining Scale, Mg Composition and Heat Treatment Conditions with Mechanical Properties in Al-7Si-Mg Cast Aluminum Alloys