PREPARATION AND MICROSTRUCTURE OF IN SITU REINFORCED Ce-TZP MATRIX COMPOSITES

叶建东,李红彦,吴建青,王迎军

DOI: https://doi.org/10.3321/j.issn:1000-3851.2002.01.012

2002-01-01

Abstract:In situ reinforcement of ceramic matrix can be achieved by the elongated grains or platelets in situ formed in matrix during sintering through the mechanisms of crack bridging, crack deflection, elongated grain/platelet pullout, etc. In this work, in situ Al2O3 platelet/Ce-TZP composites and in situ O·6Al2O3 rod-like grain/Ce-TZP composites were prepared by adding AlOOH together with the mineralizer of TiO2 or the reactant of SrCO3 to the Ce-TZP matrix. The microstructure of the composites was observed by SEM, and the density and mechanical properties of the composites were measured. Experimental results indicated that TiO2 markedly promoted the anisotropic grain growth of Al2O3 and the reaction between SrCO3 and Al2O3, forming Al2O3 platelets and anisotropic SrO·Al2O3 rod-like grains respectively. The in situ Al2O3 platelets and SrO·6Al2O3 rod-like grains were well-distributed in the matrix with a larger aspect ratio. The sintering temperature obviously affected the grain size and the content of Al2O3 platelets and SrO·6Al2O3 rod-like grains. Mechanical properties of the composites were improved by the in situ introduction of Al2O3 platelets and SrO·6Al2O3 rod-like grains.