Study on steel-Al-20Sn nonhomogeneous diffusion bonding

Peng Zhang,Yunhui Du,Daben Zeng,Jianzhong Cui,Limin Ba
2002-01-01
Abstract:An idea about nonhomogeneous diffusion which can be used to eliminate the embrittlement of steel-Al-20Sn interface was presented and realized by conducting the steel-mushy Al-20Sn rolling casting bonding. The interfacial structure was changed and the interfacial embrittlement was eliminated. Results showed that under the condition of 500°C preheat temperature on steel plate and 10 mm/s casting speed in, rolling when the solid fraction was 34.3%, the interface was made up with the right ratio Fe-Al compound and Fe-Al solid solution alternatively, and because of the elimination of interfacial embrittlement, the maximum interfacial shear strength could reach to 69.9 MPa.