Abstract:A new method for the preparation of nano-zinc oxide was proposed for the effective use of zinc oxide dust (ZOD) containing complex impurities recycled and processed from local plants. Fe2+, Fe3+, Ca2+, Mg2+, Mn2+, Cu2+, and Pb2+, Sn4+, Al3+, Si4+, Bi3+ were selectively extracted from ZOD by alkaline leaching combined with precursor firing process. The effects of thermodynamic analysis of ZOD, Sodium hydroxide(NaOH) concentration(2–8 mol/L), leaching time (15–75 min), autothermal temperature of leaching reaction (43–70 °C), leaching liquid/solid ratio (L/S:5–25 mL/g), and pH were investigated during leaching process. Thermogravimetry-differential thermogravimetry (TG-DTG) analyses were carried out on Zinc carbonate hydroxide (Zn5(CO3)2(OH)6) precursor. In addition, the effects of calcination temperature(400–700 °C) and holding time (1.5–4.0 h) of precursors on average particle size of nano-ZnO were also studied. The results showed the leaching rate of Zn2+ reached 98.35% under the optimum conditions as: NaOH concentration of 6 mol/L, L/S of 20 mL/g, and leaching time of 60 min. Separation rates of Pb2+, Sn4+, Al3+, Si4+ reached 94.63%, 85.08%, 98.03%, 91.48%, respectively at pH = 5.5. Zn5 (CO3)2(OH)6 nano precursors were obtained at pH = 7–8. After the precursor of zinc carbonate was calcined at 400–600 °C for 2 h, high purity (99.53%) nano-zinc oxide was obtained with a particle size of 20 nm, a specific surface area of 23.84 m2/g, a porosity of 32.66%, and a zeta potential of −13.2 mV. This article provides an alternative new idea for the green and comprehensive utilization of industrial ZOD dusts with complex compositions.

Electrochemical Synthesis of Zinc Complexes and Preparation of Nano-Sized ZnO

Surface Morphology, Electrochemical and Electrical Performances of ZnO Thin Films Sensitized with Ag Nanoparticles by UV Irradiation

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Systematic synthesis of ZnO nanostructures.

Studies of Electrochemical Synthesis of Ultrathin ZnO Nanorod/Nanobelt Arrays on Zn Substrates in Alkaline Solutions of Amine−Alcohol Mixtures

Controllable fabrication of various ZnO micro/nanostructures from a wire-like Zn–EG–AC precursor via a facile solution-based route

Synthesis of Zinc Oxide Nanorods from Zinc Borate Precursor and Characterization of Supercapacitor Properties

Preparation of nano zinc oxide by alkaline treatment of industrial zinc oxide dust

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Preparation of nano-ZnO by direct precipitation method under ultrasonic radiation and surface modification study

Large-Scale and Rapid Synthesis of Ultralong ZnO Nanowire Films via Anodization

Facile Solution Synthesis and Characterization of Zno Mesocrystals and Ultralong Nanowires from Layered Basic Zinc Salt Precursor

Preparation of a ZnO Nanostructure as the Anode Material Using RF Magnetron Sputtering System

Synthesis of relatively monodisperse ZnO nanocrystals from a precursor zinc 2,4-pentanedionate

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2

One-Step Hydrothermal Synthesis of Comb-Like Zno Nanostructures

A Novel Low-Temperature Chemical Solution Route for Straight and Dendrite-Like Zno Nanostructures

Preparation, Structure and Performance of Zinc Oxide with High Electrochemical Discharge Capacity

Study on Preparation of Nano-ZnO by Zinc Hypoxide in Rotary Hearth Furnace

Chemistry Preparation Technique and Progress of Nanoparticle Zinc Oxide

Efficient, One-Step Mechanochemical Process for the Synthesis of ZnO Nanoparticles