Abstract:ZnO precipitates and thin solid films were prepared, respectively, in the same solution via a modified chemical bath deposition method. In the solution with distilled water as solvent and zinc nitrate hydrate, hexamethylene tetramine as reactants, a novel microsphere with nanometer holes separated by thin flakes and ZnO hierarchical structure with rod like branches were formed after 24h at 60°C. Through controlling the deposition time and the concentration of solution, the pure porous thin solid films can be fabricated. When the citric acid as capping molecules was added into the solution, the precipitates were the pure microspheres and the ZnO hierarchical structure vanished completely. After annealing at 250°C for 1h, the thin flakes have been torn off and consisted of the small ZnO nanoparticles with the average size 10nm. The porous surface of microspheres was maintained. However, after annealing at 400°C for 1h,the microspheres have been deformed and became compact. On the other hand, the thin solid films became more exiguous with the bigger surface areas in the solution with citric acid. In the solution with methanol as solvent, the precipitates were the pure ZnO hierarchical structure with rice like branches and the porous microspheres disappeared entirely. The experimental results were studied by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), TG-DSC and the possible mechanisms about the effects of citric acid and solvent on tailoring the size and morphology of ZnO were considered.

Controllable fabrication of various ZnO micro/nanostructures from a wire-like Zn–EG–AC precursor via a facile solution-based route

Controllable Synthesis of Zno with Various Morphologies by Hydrothermal Method

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Controllable Synthesis of Zno Nanostructures by A Simple Solution Route

Control of ZnO Morphology via a Simple Solution Route

Controlled Fabrication of Nanostructured ZnO Particles and Porous Thin Films Via a Modified Chemical Bath Deposition Method

A Facile Method to Fabricate Superhydrophobic ZnO Nanostructure with Petal Effect

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Facile Solution Synthesis and Characterization of Zno Mesocrystals and Ultralong Nanowires from Layered Basic Zinc Salt Precursor

A Novel Low-Temperature Chemical Solution Route for Straight and Dendrite-Like Zno Nanostructures

Control of ZnO Morhpology by Solution Route

Controlled Fabrication of Highly Oriented ZnO Microrod/microtube Arrays on a Zinc Substrate and Their Photoluminescence Properties.

Zinc-oleate Complex As Efficient Precursor for 1-D ZnO Nanostructures: Synthesis and Properties

Fabrication of ZnO with tunable morphology through a facile treatment of Zn-based coordination polymers

Precursor‐controlled synthesis of different ZnO nanostructures by the hydrothermal method

ZnO Submicron Structures of Controlled Morphology Synthesized in Zinc-Hexamethylenetetramine-ethylenediamine Aqueous System

Controllable Synthesis of ZnO Nanostructures with Various Morphologies

A Solution-Phase Approach to the Chemical Synthesis of Zno Nanostructures Via A Low-Temperature Route

Dynamically controlled synthesis of different ZnO nanostructures by a surfactant-free hydrothermal method

Systematic synthesis of ZnO nanostructures.