Characterisation of nanosized Ce0.8Sm0.2O1.9 powder made by a modified solid state reaction

Sirong Gao,Ruiqiang Yan,Wei Lai,Zhong Lang,Xingqin Liu,Guangyao Meng

2002-01-01

Abstract:The sintering ability and electrical properties of Ce0.8Sm 0.2O1.9 (SDC) powders synthesised by using a modified solid state reaction have been examined. The particle sizes of the powders calcinated at 600 °C ∼ 1000 °C were in the range of 20 nm ∼ 100 nm. The particle size of the powder calcinated at 700°C was in the range of 20 nm ∼ 30 nm. It can produce a dense cramic (> 95% relative density) when sintered at 1400 °C for 2h. The total conductivity of the sinter measured by A.C. impedance spectroscopy technique was 0.072 S/cm at 800 °C. In addition, we also investigated the effect of small amounts (< 2 mol%) of some dopants, such as Co3O4, NiO, Fe2O 3, on the sintering characteristics of this powder. About 0.5mol% Co3O4 doped SDC sintered at 1200 °C for 2h reaches almost full densification (> 98% relative density). Conductivity measurements at different temperatures revealed that for doping levels below 2mol% the conductivity of the specimen remains unchanged compared to the undoped SDC. Similar results hold for NiO and Fe2O3 as dopants in concentration ≤ 1mol%.