Preparation of Ultra-Fine Sm0.2Ce0.8O1.9 Powder by a Novel Solid State Reaction and Fabrication of Dense Sm0.2Ce0.8O1.9 Electrolyte Film

B. Zhao,Y. Tong,Y. Zhao,T. Yang,F. Yang,Q. Hu,C. Zhao

DOI: https://doi.org/10.1016/j.ceramint.2015.04.037

IF: 5.532

2015-01-01

Ceramics International

Abstract:A novel solid state reaction was adopted to prepare Sm0.2Ce0.8O1.9 (SDC) powder. A mixed oxalate Sm0.2Ce0.8(C2O4)1.5·2H2O was synthesized by milling a mixture of cerium acetate hydrate, samarium acetate hydrate, and oxalic acid for 5h at room temperature. An ultra-fine SDC powder with the primary particle size of 5.5nm was obtained at 300°C. The ultra-low temperature for the formation of SDC phase was due to the atomic level mixture of the Sm3+ and Ce4+ ions. The crystal sizes of SDC powders at 300°C, 550°C, 800°C, and 1050°C were 5.5nm, 11.4nm, 24.1nm and 37.5nm, respectively. The sintering curves showed that the powder calcined at lower temperature was easier to be sintered owning to its smaller particle size. A solid oxide electrolytic cell (SOEC), comprising porous La0.8Sr0.2Cu0.1Fe0.9O3−δ (LSCF) for substrate, LSCF–SDC for active electrode, SDC for electrolyte, and LSCF–SDC for symmetric electrode, was fabricated by dip-coating and co-sintering techniques. An extremely dense SDC film with the thickness of 20μm was obtained at only 1200°C, which was about 100–300°C lower than the literatures׳ reports. The designed SOEC was proved to work effectively for decomposing NO (3500ppm, balanced in N2), 80% NO can be decomposed at 600°C.