Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Preparation of Porous Zro2 and Study on Its Properties

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation and Characterization of Crox/Zro2 with High Thermal Stability and High Specific Surface Area

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Preparation of Zirconia Powders by Sol-gel Process

Preparation of High-Surface-Area Sno2 and Zro2 by Reflux-Digestion and Solvothermal Methods

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Preparation and Characterization of Mesoporous Tetragonal Sulfated Zirconia

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Synthesis of Ordered Hexagonal Porous Tin-Doped Zirconium Oxides with a High Surface Area

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Preparation of Ultrafine Ce-Zr-Ba Mixed Oxide Powder with High Surface Area

Preparation of High Surface Area Zirconia by RefluxDigestion in Basic Solutions

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Preparation and Characterization of Mesoporous Zirconia Materials by Self-Assembly Method

Preparation and characterization of metal oxide supported silica pillared zirconium phosphates with high surface area

Preparation of a high surface area zirconium oxide for fuel cell application

Preparation of macroporous zirconia monoliths from ionic precursors via an epoxide-mediated sol-gel process accompanied by phase separation

Synthesis of porous ZrC particles derived from MOF-801

Sol–gel Synthesis of Mesoporous Spherical Zirconia