Investigation on Tree Initiation in Polyethylene Films Exposed to Thermo-oxidation
Ping Yan,Yuanxiang Zhou,Noboru Yoshimura
DOI: https://doi.org/10.1541/ieejfms1990.120.6_718
2000-01-01
Abstract:Treeing phenomena, which occur in polymer dielectrics, have been widely studied for many years (1. 2). The tree, once generated, will grow with intermal discharge, and eventually bridge the electrodes, resulting in a complete breakdown. Though thermal oxidation of polyethylene (PE) has been the subject of numerous investigations (3,4), we still lack of database on relating oxidation of PE to tree initiation phenomena. It is well known that electrical properties depend to a great extent on morphology, oxidation and contamination. Recent studies show that the electrical properties of polyethylene, such as breakdown strength and tree initiation voltage, increase with the increase of crystallinity (or density) (5-8). It has also been demonstrated that morphology of PE is considerably changed after oxidizing(9). However, the detail process of morphological change due to oxidation and its influence on tree initiation is far from being understood. In this paper, morphological changes and tree initiation of highdensity polyethylene (HDPE) and low-density polyethylene (LDPE) films after thermo-oxidizing were studied. It was shown that crystallinity and value of tree initiation voltage increase when PE films were oxidized during a certain period of time. It was recognized that thermo-aging, as a complex process, shows a few benefits in spite of some detrimental consequences, depending on the aging conditions. 2. Experimental 2.1 Materials Two kinds of non-additive PE polymers, they were HDPE and LDPE, were used in our experiments. Table I shows the physical properties of these polymers. HDPE has a linear macromolecular chain structure and a few chain branches. By comparison to LDPE, it has a better tacticity, a lager density and a higher crystallinity. Because LDPE consists of many long or short chain branches such as methyl, ethyl, and butyl, the tacticity of LDPE is not good, and its crystallinity and density are low.