Electrical Treeing Behavior in Polyethylene Filled with Aluminum Oxide Nanoparticles

Deni Murdany,Xiangrong Chen,Mattias Andersson,Dongmin Liu,Ulf Gedde,Stanislaw Gubanski

DOI: https://doi.org/10.5324/nordis.v0i24.2277

2017-01-01

Proceedings of the Nordic Insulation Symposium

Abstract:Electrical treeing behavior in low density polyethyleneand its nanocomposite filled with 1.0 wt% and 3.0 wt%aluminum oxide nanoparticles was investigated bymeans of a real-time microscope recording system and asynchronized partial discharge measurement. Forpreparing the nanocomposite, uncoated aluminum oxidenanoparticles with 99.5% purity (Nanodur, CAS 1344-28-1) were used. These were of almost spherical shapewith an average diameter of 45 nm. The test objectswere prepared in form of the wire-plane electrodegeometry [1]. The electrical treeing tests were carriedout by applying 50 Hz AC voltage at a ramping speed of22 V/s. The obtained experimental results indicate thatthe addition of the nanoparticles has a positive impacton the resistance to electrical treeing. Both the scale andthe shape of the distribution of the treeing initiationvoltage improved. The magnitude of partial dischargeactivity associated with the treeing in polyethylenenanocomposites was also lower than in the referencematerial.