Abstract:Conducting polypyrrole (PPy) films doped with p-toluenesulfonate (TOS−), ClO4−, and Cl− were electrochemically prepared, respectively. The electrochemical capacitance properties of the PPy films were investigated with cyclic voltammetry (CV), galvanostatical charge/discharge, and electrochemical impedance spectroscope (EIS) techniques. The morphology observation and structure analysis of PPy films were performed by scanning electron microscope (SEM) and X-ray diffraction (XRD). The results showed that PPy-Cl and PPy-TOS were characterized with a highly porous and ordered structure, which led to their fast ion switch processes. Moreover, they exhibited a rectangle-like shape of voltammetry characteristics even at a scanning rate of 50 mV·s−1, a linear variation of the voltage with respect to time in the charge/discharge process, and almost ideal capacitance behavior in low frequency, even in deeply charged/discharged states in 1 mol·L−1 KCl solution. Furthermore, specific capacitance of PPy-Cl (polymerization charge of 2 mAh·cm−2) could reach 270 F·g−1 (scanning rate of 5 mV·s−1) or 175 F·g−1 (scanning rate of 200 mV·s−1) and its specific energy could reach 35.3 mWh·g−1. Moreover, with heavier doping ion (TOS−), PPy-TOS (polymerization charge of 2 mAh·cm−2) had a slightly smaller specific capacitance (146 F·g−1, scanning rate of 5 mV·s−1), but a very rapidly charge/discharge ability (specific capacitance of 123.6 F·g−1 at scanning rate of 200 mV·s−1) and its specific power could reach 10 W·g−1. In addition, both PPy-TOS and PPy-Cl had good cycleability. All of the above implied that the PPy-Cl and PPy-TOS were two kinds of promising electrode material for supercapacitors.

Influence of Electropolymerization Conditions on the Capacitance and Dissipation Factor of Polypyrrole Tantalum Electrolytic Capacitors

Influence of Conductive Polymer(PEDT) on Performance of Tantalum Electrolytic Capacitors

Investigation of Production Process of Polymer Solid Electrolyte Tantalum Capacitor Based on High Specific Surface Area Tantalum Powder

Chemical Synthesis of Conducting Poly(3,4-Ethylenedioxythiophene) (PEDT) Film on the Surface of Anode of Solid Tantalum Electrolytic Capacitor

Vapor Phase Polymerization Deposition Conducting Polymer Nanocomposites on Porous Dielectric Surface As High Performance Electrode Materials

Research on Production Process of Polymer Electrolyte Tantalum Capacitors

Capacitance Properties of Poly(3,4-Ethylenedioxythiophene)/polypyrrole Composites

Effect of Doping Ions on Electrochemical Capacitance Properties of Polypyrrole Films

Semitransparent, Flexible Electrochemical Capacitors with Excellent Stability Fabricated with Polypyrrole–titanium Mesh Electrodes

Performance of Flexible Capacitors Based on Polypyrrole/Carbon Fiber Electrochemically Prepared from Various Phosphate Electrolytes

Investigation of Conducting Poly(3,4-Ethylene Dioxy Thiophene) Film on Surface of Tantalum/Tantalum Pentoxide-Based Anode

In situ electrodeposition of polypyrrole onto TaSe2 nanobelts quasi-arrays for high-capacitance supercapacitor.

Preparation of the Flexible Polypyrrole/Polypropylene Composite Fibrous Film for Electrochemical Capacitor

Influence of Impregnation Technology on the Property of Winding-Solid Polypyrrole Aluminum Electrolytic Capacitor

Flexible Electrochemical Capacitors Based on Polypyrrole/carbon Fibers Via Chemical Polymerization of Pyrrole Vapor

Electrodeposition and capacitive behavior of films for electrodes of electrochemical supercapacitors

Effects of Additives on Properties of Polypyrrole Solid-Chip Aluminum Electrolytic Capacitors

Influence of Dipping Conditions on the Rate of Capacitance Withdrawing of Solid Electrolytic Aluminum Capacitor Using PEDOT As Conducing Cathodal Layer

Self-healing Solid Tantalum Electrolytic Capacitors with Low ESR, High-Frequency Performance, and Simple Fabrication

Electrical Performance Enhancement of 400 V Level Aluminum Solid Electrolytic Capacitors with Interface Modulation Through Intervention of PVA

Preparation and Capacitive Property of Polypyrrole Deposited on the Flexible Polypropylene Fibrous Films