Performance-enhanced cholesterol biosensor based on biocomposite system: Layered double hydroxides-chitosan
Shou-Nian Ding,Dan Shan,Tao Zhang,Yan-Zhi Dou
DOI: https://doi.org/10.1016/j.jelechem.2011.04.003
IF: 4.598
2011-01-01
Journal of Electroanalytical Chemistry
Abstract:Using layered double hydroxides (LDHs)-chitosan (Chit) composite as enzyme immobilization matrix, the developments of cholesterol biosensor were achieved by both electrooxidation and electroreduction of the enzymatic-generated hydrogen peroxide based on cholesterol oxidase (ChOx) and horseradish peroxidase (HRP). Amperometric detection of cholesterol was evaluated by holding the modified electrode at 0.55 V and 0 V (vs. SCE), for ChOx/LDHs-Chit/Pt and ChOx/HRP/LDHs-Chit/GCE, respectively. The linear dynamic ranges of anodic and cathodic detections of cholesterol were between 5 × 10 −7 to 8 × 10 −4 M and 4 × 10 −8 to 6 × 10 −4 M, respectively. The detection limits were determined to be of 1 × 10 −7 and 4 × 10 −8 M with anodic and cathodic processes, respectively. At potential of 0 V, ChOx/HRP/LDHs-Chit/GCE bienzymatic mediated system exhibited excellent selectivity and stability. Keywords Cholesterol oxidase Horseradish peroxidase Layered double hydroxides Chitosan Cholesterol Biosensor 1 Introduction Cholesterol and its fatty acids are important components of nerve and brain cells and are precursors of biological substances, such as bile acid and steroid hormones [1] . The balanced quantity of cholesterol in blood provides durability and integrity to the cell architecture. However, its elevated levels are associated with atherosclerosis, nephrosis, diabetes milletus, myxedema, jaundice and decreased levels may result in hyperthyroidism, anaemia and maladsorption [2,3] . Hence cholesterol determination is of great importance for clinical applications. Biosensors have recently gained much attention in the field of health care for the management of various important analytes in a biological system [4] . Among them, ChOx-based electrochemical biosensors have gained the tremendous progress for the determination of cholesterol [5–10] . Compared with other analytical techniques, such sensors possess simplicity of operation and the substrate selectivity of the enzymes. In addition, they are inexpensive since a small amount of immobilized enzyme (ChOx) can be used for a large number of analytical determinations. In most of conventional cholesterol sensors, ChOx catalyzes the conversion of cholesterol into 5-cholesten-3-one and hydrogen peroxide in the presence of oxygen, which can be detected amperometrically. However, several interfering compounds can contribute to the biosensor response due to the high potential usually required for H 2 O 2 detection. Therefore the development of high-performance cholesterol biosensor has been a focal subject in bioanalytical science and technology. In our previous works, layered double hydroxides (LDHs), have been demonstrated as attractive enzyme immobilization matrix [11–14] . LDHs display a layered structure built on a stacking of positive layers ([M 1− x II M x III (OH) 2 ] x + [15] . The electroneutrality of the system can be realized by the presence of changeable anions accompanied with water molecules situated in the interlamellar domains. Furthermore, the properties of LDHs can be efficiently improved by introduction biopolymer such as chitosan (Chit) [16,17] and alginate [18] . The biopolymer in the clay composite can not only overcome the brittleness of the pure clay film, but also increase the biocompatibility and the adhesive ability of the composite film to the electrode surface, resulting in the improved analytical performance of the biosensor. Moreover, the usage of glutaraldehyde, which can denature the enzyme, could be finally avoided [16–20] . This contribution describes the extended application of LDHs-Chit composite as enzyme immobilization matrix to construct highly performance-enhanced cholesterol biosensor. Two different enzyme systems have been checked involving monoenzyme ChOx on the one hand, and bienzyme ChOx/HRP coimmobilization, on the other hand. The analytical performance of the biosensors derived from both enzyme systems has been evaluated. 2 Experimental 2.1 Materials Cholesterol oxidase (ChOx) (EC1.1.3.6, 8.1 U mg −1 ) was obtained from Sigma. Horseradish peroxidase (HRP) (EC 1.11.1.7, type II, 140 U mg −1 ), cholesterol, brilliant cresyl blue (BCB), azure B and ferrocenemethanol (MeOHFc) were purchased from Amresco. Chitosan (CHT, MW ∼1 × 10 6 ; >90% deacetylation) Layered double hydroxides (LDHs) Zn 3 Al(OH) 8 Cl, denoted [Zn 3 –Al–Cl] was synthesized by coprecipitation method developed by De Roy [14,15] . All other reagents were of analytical grade and used as received without further purification. All aqueous solutions were prepared in deionized distilled water. Phosphate buffer (0.1 M) (pH 7.0) was used for all the experiments unless otherwise indicated. 2.2 Measurements and apparatus All electrochemical studies were performed with a conventional three-electrode system. A saturated calomel electrode (SCE) and a Pt foil electrode were used as reference electrode and counter electrode, respectively. The working electrode was a platinum disk electrode (diameter 2 mm) or glassy carbon electrode (diameter 3 mm), polished carefully with 0.05 μm alumina particles on silk followed by rinsing with the distilled water and dried in air before use. All measurements were carried out in a thermostated cell at 25 °C, containing phosphate buffer solution. 2.3 Preparation of enzyme electrodes A 2.0-wt% Chit solution was prepared by dissolving Chit flakes in 1.0-wt% acetic acid (HAc), and was then diluted into 0.2-wt% solution (about pH 4.0) by adding water. The LDHs [Zn 3 –Al–Cl] colloidal suspension (2 mg ml −1 ) was prepared by dispersing LDHs in deionized and decarbonated water stirring overnight. ChOx or HRP was also dissolved in deionized water with a concentration of 2 mg ml −1 . A defined amount of aqueous enzyme/LDHs-Chit mixture (for instance, containing 16 μg [Zn 3 –Al–Cl], 4 μg Chit and 20 μg enzyme) was spread on the surface of the platinum disk electrode or glassy carbon electrode. The coating was then dried at 4 °C in a refrigerator for overnight, leading to adherent LDHs/Chit film in which enzymes were entrapped. Before use, the enzyme electrode was rinsed under stirring for 20 min with buffer solution to remove the enzyme not firmly immobilized. 3 Results and discussion 3.1 ChOx/LDHs/Pt monoenzymatic system ChOx belongs to the family of oxidoreductases, specifically those acting on the CH–OH group of donor with oxygen as acceptor, which catalyzes the chemical reaction (as shown in Inset I of Fig. 1 ): cholesterol + O 2 cholest- 4 -en - 3 -one + H 2 O 2 As a consequence, the amperometric detection of cholesterol was assayed by potentiostating the ChOx/LDHs-Chit/Pt electrode at 0.55 V to oxidize the enzymatically generated hydrogen peroxide. ChOx/LDHs-Chit/Pt shows a rapid response to cholesterol (<6 s). Such a rapid response indicates a fast mass transfer of the substrate across the film and a fast electron exchange between ChOx and its substrates, highlighting the advantages of LDHs-Chit composite as host matrix for the construction of the biosensor. Inset II of Fig. 1 shows a typical calibration graph of ChOx/LDHs-Chit/Pt bioelectrode for the determination of cholesterol. It appears that the linear part of the calibration curve overlays a range of cholesterol concentration: from 0.5 to 800 μM with a correlation coefficient of 0.998 ( n = 10) and a detection limit of 0.1 μM cholesterol determined at a signal-to-noise ratio of 3. The cholesterol sensitivity is calculated to be 10.4 mA cm −2 M −1 . The effect of temperature on the ChOx/LDHs-Chit/Pt bioelectrode response to 0.1 mM cholesterol was evaluated between 10 and 55 °C. The current response gradually increases with increasing temperature and reaches a maximum at 50 °C (Curve a in Fig. 1 ). This value is greater than that observed for modified ChOx/Pt electrode in the absence of LDHs-Chit (Curve b in Fig. 1 ). Such a high optimal temperature of the running of the bioelectrode may be ascribed to the beneficial effect brought by LDHs-Chit as the enzyme host matrix. In the LDHs-Chit composite, the highly hydrophilic LDHs in this hybrid system can prevent the enzyme from thermal denaturation, simultaneously, the highly biocompatible Chit can further improve the biocompatibility of the host matrix, providing a friendly microenvironment for the entrapped enzyme. 3.2 ChOx/HRP/LDHs-Chit/GCE bienzymatic system 3.2.1 Selection of mediator To eliminate the interferences and improve the biosensor selectivity, an alternative approach was performed by enzyme-channeling assay [13,21] . Thus, the construction of bienzymatic ChOx/HRP amperometric biosensor was applied for cholesterol detection. Fig. 2 A shows the functioning principle of the composite biosensor based on the co-immobilization of ChOx and HRP within the LDHs-Chit hybrid matrix. In such configurations, H 2 O 2 produced by ChOx-cholesterol-dissolved oxygen system is detected through its HRP-mediated reduction, which might permit the detection of cholesterol at low potential and can avoid the interference of the coexisting electroactive substances. Three mediators, namely, Brilliant cresyl blue (BCB), azure B and ferrocenemethanol (MeOHFc), were investigated for this ChOx-HRP bienzymatic system for cholesterol. BCB and azure B belong to phenothiazine and methylated thiazine dyes, respectively. They are charged positively. However, MeOHFc is charged neutrally. As shown in curve a of Fig. 2 B, C and D, in the absence of the cholesterol, the anodic and cathodic voltammetric peaks, are attributed to the redox signal of the corresponding mediator. But in the presence of 0.1 mM cholesterol, the cyclic voltammogram displays an enhancement of the cathodic peak current and a concomitant decrease of the anodic peak current (curve b of Fig. 2 B–D). This suggests that cholesterol could be oxidized catalytically at the ChOx/HRP/LDHs-Chit /GCE-mediated system. Compared among the above-mentioned mediators, MeOHFc as mediator can realize the detection of cholesterol at 0 V vs. SCE. Thus, MeOHFc was selected in this ChOx/HRP/LDHs-Chit/GCE-mediated system. 3.3 MeOHFc mediated bienzymatic system for cholesterol detection Fig. 3 depicts typical cyclic voltammograms of bienzyme sensor in 0.1 M PBS (pH = 7 containing 0.1 mM MeOHFc at different scan rate. The plots of the peak current ( i p ) against ν 1/2 according to the Randles–Sevick equation demonstrate the strong linear relationships ( R 2 = 1, for both i pa ∼ ν 1/2 and i pc ∼ ν 1/2 , respectively) for this bienzyme-MeOHFc system (inset of Fig. 3 ). The linear behavior of the peak current with the square root of scan rate indicates that the redox behavior of the electrode is diffusion controlled. Thus, the oxidized and reduced forms of MeOHFc in the solution are not adsorbed on ChOx/HRP/LDHs-Chit-modified GCE. Since ChOx catalyzes the aerobic oxidation of cholesterol with concomitant production of H 2 O 2 , the amperometric response of the bienzymatic ChOx/HRP/LDHs-Chit/GCE to cholesterol was also investigated in this present work. The dependence of the MeOHFc-mediated bienzyme electrode response on the applied potential was evaluated over the potential range from −0.15 to 0.1 V for cholesterol in 0.1 M PBS (pH 7.0) ( Fig. 4 ). The optimal applied potential can be observed at 0 V vs. SCE. Consequently, an operational potential value of 0 V was chosen for subsequent amperometric measurements for cholesterol. Fig. 5 displays the typical amperometric response of the biosensor based on bienzyme-MeOHFc sensing system for successive injection of cholesterol to stirring 10 ml 0.1 M PBS at pH 7.0. The response current of the biosensor is linear in the range from 4 × 10 −8 to 6 × 10 −4 M with a low detection limit of 4 × 10 −8 based on signal/noise = 3 and a correlation coefficient of 0.997 ( n = 30). The analytical performances of the proposed biosensor were compared with those cholesterol sensors, as summarized in Table 1 . It appears that the relative low detection limit was obtained with the ChOx/HRP/LDHs-Chit/GCE-MeOHFc system. This improved detection limit can be also ascribed to the low applied potential which provided low background current. 3.4 Stability for the MeOHFc-mediated bienzyme electrode to cholesterol The reproducibility of the analytical responses obtained from different electrodes constructed by the same procedure was analyzed. Seven different electrodes were tested independently for these amperometric responses to 0.1 mM cholesterol. The results revealed that the relative standard deviation (RSD) value for all seven electrodes was 5.6%. Both operational and long-term storage stability are very important form the pratical application point of view [19] , so these two parameters were also examined. The operational stability of the ChOx/HRP/LDHs-Chit/GCE-MeOHFc mediated system was examined. A reproducible current response with a RSD of 3.0% was observed in 60 successive assay of 0.1 mM cholesterol ( Fig. 6 A). The long-term stability of this proposed mediated bienzymatic system was also investigated by recording periodically. Its biosensor retained 92.8% and 62.5% of its cholesterol sensitivity after 14 and 40 days, respectively ( Fig. 6 B). This good stability reflects the biocompatibility of the LDHs-Chit composite and its efficient retention properties towards enzyme molecules. 3.5 Interference study The interferences of electroactive species to the cholesterol response were examined in the presence of their physiological normal levels with cholesterol concentration at 0.1 mM [22,23] . Interference was estimated as the percentage increase in the biosensor signal recorded in the presence of interferents compared with the stead-state biosensor response to 0.1 mM cholesterol alone. The influences of ascorbic acid (0.1 mM), p -acetamidophenol (0.05 mM), l -cysteine (0.02 mM), glucose (5.6 mM), and reduced glutathione (2 mM) were estimated in this work with two cholesterol sensors, namely, the monoenzymatic electrode (ChOx/LDHs-Chit/Pt applied at 0.55 V vs. SCE) and mediated bienzymatic system (ChOx/HRP/LDHs-Chit/Pt-MeOHFc). The results are illustrated in Fig. 7 . The influence of ascorbic acid, p -acetamodophenol, l -cysteine, glucose and reduced glutathione were effectively reduced with the mediated bienzymatic system (ChOx/HRP/LDHs-Chit/GCE-MeOHFc). This is ascribed to the efficiency of the electrocatalytic process in the whole structure of LDHs-Chit matrix and also to the value of the low operating potential of 0 V vs. SCE. 4 Conclusion The development of amperometric biosensor for monitoring cholesterol was described in this paper. Due to the satisfactory biocompatibility, attractive interfacial properties, LDHs-Chit was further confirmed as a host enzyme immobilization matrix for constructing both monoenzymatic and multienzymatic biosensors. Cholesterol sensor based on LDHs-Chit exhibited the highly developed analytical performance to cholesterol such as rapid response, high sensitivity and good stability. In addition, the proposed cholesterol biosensor by coupling of HRP with ChOx permitted the selective detection of cholesterol at 0 V vs. SCE and could avoid the interference of coexisting substances. Acknowledgements The authors are grateful to the financial supports of National Natural Science Foundation of China (Grant Nos. 20905011, 21010102071), the Natural Science Foundation of Jiangsu (No. BK2010396), University science research project of Jiangsu Province (09KJB150015), and the Open Research Fund of State Key Laboratory of Bioelectronics, Southeast University. This work was also supported by the Southeast University Creative Foundation (3207040501). References [1] S. Aravamudhan A. Kumar S. Mohapatra S. Bhansali Biosens. Bioelectron. 22 2007 2289 2294 [2] M. Nauck W. März H. Wieland Clin. Chem. 46 2000 436 437 [3] V. Malik C.S. Pundir Biotechnol. Appl. Biochem. 35 2002 191 197 [4] S.K. Arya M. Datta B.D. Malhotra Biosens. Bioelectron. 23 2008 1083 1100 [5] A.I. Gopalan K.P. Lee D. Ragupathy Biosens. Bioelectron. 24 2009 2211 2217 [6] W.C. Shih M.C. Yang M.S. Lin Biosens. Bioelectron. 24 2009 1679 1684 [7] C. Dhand S.K. Arya S.P. Singh B.P. Singh M. Datta B.D. Malhotra Carbon 46 2008 1727 1735 [8] A. Kaushik P.R. Solanki K. Kaneto C.G. Kim S. Ahmad B.D. Malhotra Electroanalysis 22 2010 1045 1055 [9] Z. Matharu G. Sumana S.L. Arya S.P. Singh V. Gupta B.D. Malhotra Langmuir 23 2007 13188 13192 [10] Z. Matharu S.K. Arya S.P. Singh V. Gupta B.D. Malhotra Anal. Chim. Acta 634 2009 243 249 [11] D. Shan S. Cosnier C. Mousty Anal. Chem. 75 2003 3872 3879 [12] D. Shan C. Mousty S. Cosnier Anal. Chem. 76 2004 178 183 [13] D. Shan S. Cosnier C. Mousty Anal. Lett. 36 2003 909 922 [14] D. Shan W.J. Yao H.G. Xue Electroanalysis 18 2006 1485 1491 [15] A. De Roy, C. Forano, K. El Malki, J.P. Besse, Expanded clays and other microporous solids, in: M.L. Occelli, H.E. Robson (Ed.), Expanded clays and other microporous solid, Van Nostrand Reinhold, New York, 1992, pp. 108–169. [16] E. Han D. Shan H.G. Xue S. Cosnier Biomacromolecules 8 2007 971 975 [17] Q.F. Shi E. Han D. Shan W.J. Yao H.G. Xue Bioprocess Biosyst. Eng. 31 2008 519 526 [18] S.N. Ding D. Shan H.G. Xue D.B. Zhu S. Cosnier Y.M. Sun Anal. Sci. 25 2009 1421 1425 [19] Q. Fan D. Shan H.G. Xue Y.Y. He S. Cosnier Biosens. Bioelectron. 22 2007 816 821 [20] Q.F. Shi Q.B. Li D. Shan Q. Fan H.G. Xue Mater. Sci. Eng. C 28 2008 1372 1375 [21] S. Cosnier C. Mousty X.Q. Cui X.R. Yang S.J. Dong Anal. Chem. 78 2006 4985 4989 [22] D. Shan M.J. Zhu H.G. Xue S. Cosnier Biosens. Bioelectron. 22 2007 1612 1617 [23] D. Shan Y.Y. He S.X. Wang H.G. Xue H. Zheng Anal. Biochem. 356 2006 215 221 [24] C.Z. Zhao L. Wan L. Jiang Q. Wang K. Jiao Anal. Biochem. 383 2008 25 30 [25] K.M. Manesh P. Santhosh A.L. Gopalan K.P. Lee Electroanalysis 22 2010 2467 2474 [26] H. Ohnuki R. Honjo H. Endo T. Imakubo M. Izumi Thin Solid Films 518 2009 596 599