Abstract:Detailed NMR investigations on fresh and coked Mo/HMCM-22 catalysts for methane dehydro-aromatization were presented. Al-27 MAS and Si-29 MAS as well as corresponding CP/MAS NMR experiments have proved that an interaction between molybdenum and the zeolite lattice occurs during the impregnation and calcination processes of the catalysts. With Bronsted acid sites serving as a powerful trap, molybdenum migrates into the internal channels of the zeolite and reacts preferentially with bridging hydroxyls groups. Thus, molybdenum is anchored to the framework aluminum through an oxygen bridge, which, in turn, modifies the acidic properties of the HMCM-22 and leads to a high dispersion of the molybdenum. If this kind of interaction becomes stronger, expelling of aluminum from the zeolite lattice would occur, with the forming of both octahedral nonframework aluminum and Al-2(MoO4)(3) crystallites, The latter can be hydrated to [Al(OH)(n)(H2O)(6-n)](n)(MoO4) (n = 1 or 2) in a water-saturated desiccator and can give a line at ca. 14 ppm in the Al-27 MAS NMR spectrum. UV-Raman results suggest that the carbonaceous deposits on the catalysts are mainly hydrogen-deficient aromatic type, which are also verified by H-1 --> Si-29 CP/MAS and H-1 --> Al-27 CP/MAS NMR, as well as the failure for conducting the C-13 CP/MAS NMR experiment. H-1 --> Al-27 CP/MAS NMR experiments indicate that most of the coke is deposited on framework aluminum (Bronsted site). Regeneration in an oxygen atmosphere leads to the formation of a considerable amount of Al-2(MoO4)(3) crystallites. However, the catalytic activity can be properly restored after the regeneration; thus, the idea of taking this species as the detrimental factor for this reaction can be ruled out. On the other hand, lattice destruction of the zeolite is suggested to be responsible for the poor performance exhibited by the 10Mo/HMCM-22 catalyst. The synergic effect between molybdenum and Bronsted acid sites is considered to be the main reason for the outstanding catalytic performance of the 6Mo/HMCM-22 catalyst.

XAFS Study of Silica-supported Chromium-based Catalyst

Simultaneous Conversion of Methane and Carbon Dioxide to Aromatics over Silica Supported Chromium-Based Catalysts

Catalytic Performance of Au III Supported on SiO 2 Modified Activated Carbon

Chromium-based Catalysts for Ethane Dehydrogenation: Effect of SBA-15 Support

Catalytic properties and nature of active centers of Cr/MCM-41 in catalytic abatement of sulfur-containing VOC of methanethiol

Effect of synthesis parameters on the chromium content and catalytic activities of mesoporous Cr-MSU-x prepared under acidic conditions

Study on Silica Supported Cu Cr Mo Nitrobenzene Hydrogenation Catalysts

High-resolution 29 Si CP/MAS Solid State NMR Spectroscopy and DFT Investigation on the Role of Geminal and Single Silanols in Grafting Chromium Species over Phillips Cr/silica Catalyst

Esr Study On The Nature Of Active Site Of Silica-Supported Chromia In Propane Dehydrogenation Reaction

Catalytic performance of silica-supported chromium oxide catalysts in ethane dehydrogenation with carbon dioxide

Synthesis, Characterization and Catalytic Evaluation of Chromium Oxide Deposited on Titania–Silica Mesoporous Nanocomposite for the Ethane Dehydrogenation with CO2

Oxidative Dehydrogenation of Ethane with Co2 over Cr Supported on Submicron Zsm-5 Zeolite

Clarification of Active Sites at Interfaces Between Silica Support and Nickel Active Components for Carbon Monoxide Methanation

Single Chromium Atoms Supported on Titanium Dioxide Nanoparticles for Synergic Catalytic Methane Conversion under Mild Conditions

Cr/ZSM-5 for Ethane Dehydrogenation: Enhanced Catalytic Activity Through Surface Silanol

Screening silica-confined single-atom catalysts for nonoxidative conversion of methane

Chromium Oxide Supported on Silicalite-1 Zeolite As a Novel Efficient Catalyst for Dehydrogenation of Isobutane Assisted by CO2

Mo/HMCM-22 Catalysts for Methane Dehydro-Aromatization: A Multinuclear MAS NMR Study

Development of a robust sulfur quantification and speciation method for SBA-15-supported sulfonic acid catalysts

Visualization of the Active Sites of Zinc-Chromium Oxides and the CO/H2 Activation Mechanism in Direct Syngas Conversion

Effect of supports on the catalytic performance of chromium oxide catalysts for the coupling of reversed water-gas shift reaction with the dehydrogenation of ethane to ethylene