Effects of Transition Metals, Fe, Ni, Sc and Zr, on the Microstructure and Mechanical Properties of 2618 Aluminum Alloy

Kun Yu,Songrui Li,Wenxian Li

2000-01-01

Rare Metal Materials and Engineering

Abstract:Three Al-Cu-Mg-Fe-Ni-(Sc, Zr) alloys with different compositions have been prepared. The age hardening curves of the alloys at 200 degrees C were measured using vickers hardness, and the tensile properties at both ambient temperature (20 degrees C) and 300 degrees C were also measured. The microstructures of the alloys were observed using optical microscopy, SEM and TEM. It was found that additions of Sc and Zr to 2618 alloy resulted in a primary Al-3 (Sc,Zr) phase which could refine the grain size and a uniform distribution of secondary coherent Al-3 (Sc, Zr) particles which had an obvious age hardening effect. The dispersed Al-3 (Sc, Zr) precipitates could homogenize the S' phase precipitate such that the strength of the alloy increased at both ambient and elevated temperatures without decreasing ductility. Increasing the Fe and Ni content resulted in an insoluble phase, AlCuFeNi, which produce precipitate strengthening effect and decreased the a mount of S' phase. Thus the mechanical properties, especially the strength, of the alloy with high percent ages of Fe and Ni were not greatly improved.