Abstract:A novel hyperbranced azo polymer with terminal diazonium groups was synthesized by step-growth polymerization of 4,4'-diamino diphenyl sulphone's diazonium salts (A(2)) and benzene-1,3,5-triearboxylic acid tri2-(N-ethylanilino) ethyl ester (B-3) through azo-coupling reaction. 4, 4'-diamino diphenyl sulphone (0.248 g, I mmol) was dissolved in a hot homogeneous mixture of glacial acetic acid (7.5 mL) and sulfuric acid ( I mL). Aqueous solution of sodium nitrite (0.166 g, 2.4 mmol) in 0.5 mL water was added dropwise into the solution at 0 degrees C and kept at this temperature for 5 min. The diazonium salt solution of 4,4'-diamino diphenyl sulphone was then added dropwise into the solution of benzene-1, 3, 5-tricarboxylic acid tri-2-( N-ethylanilino) ethyl ester (0.326 g, 0.5 mmol) in 50 mL DMF at 0 degrees C. After the reaction was carried out at 0 degrees C for 8 h, the solution containing the diazonium-hyperbranched azo polymer was directly used as the polyeation solution. The purchased sodium polystrene sulfonate (PSSA) was used as polyanion. Then the multilayer films were prepared by an electrostatic layer-by-layer deposition method. The self-assembly processes and morphologies of surfaces were characterized by UV-Vis spectra, ellipsometer and AFM. A linear increase of absorbance and thickness was observed as the number of the bilayers increased. Dichroism was optically induced in the self-assembly film under the irradiation of a polarized Ar+ laser beam at 488 nm. After 15 min irradiation of the laser beam at an intensity of 80 mW/cm(2) the orientation order parameter of the multilayer film obtained was about 0.02. With interfering illumination of Ar+ laser beams for 30 min, significant surface relief gratings formed on the self-assembly multilayer film were observed. The spatial period and height of the obtained SRGs were about 744 nm and 20 nm. respectively.

Photoresponsive Self-Assembled Multilayers Of Three New Azo Polyelectrolytes.

Synthesis, Photoresponsive Behavior, and Self-Assembly of Poly(Acrylic Acid)-Based Azo Polyelectrolytes

Electrostatic Self-Assembled Multilayers from Side Chain Azo Polyelectrolytes

Polymer Micelles As Building Blocks For The Incorporation Of Azobenzene: Enhancing The Photochromic Properties In Layer-By-Layer Films

Sequentially Adsorbed Electrostatic Multilayers of Polyaniline and Azo Polyelectrolytes

Layer-By-Layer Self-Assembly and Photo-Induced Dichroism of A Novel Side-Chain Azo Polyelectrolyte

Layer-by-layer Ultrathin Films of Azobenzene-Containing Polymer/layered Double Hydroxides with Reversible Photoresponsive Behavior.

Aggregation and photo responsive behavior of azo polyelectrolytes in aqueous media

Photo-responsive supramolecular self-assembly and disassembly of an azobenzene-containing block copolymer

Selectively Erasable Multilayer Thin Film By Photoinduced Disassembly

Study on Photodynamic and Photoresponsive Azo Polyelectrolytes

Self-assembly and photoresponsive behavior of amphiphilic diblock copolymers containing azobenzene moieties

Preparation of Multicolor Electrochromic Polymer Composite Film with Laminated Structure

Self-Assembly and Optical Properties of Poly(Acrylic Acid)-Based Azo Polyelectrolyte

Tuning self-assembly and photo-responsive behavior of azobenzene-containing triblock copolymers by combining homopolymers

Synthesis and Properties of A Novel Side-Chain Azo Polyelectrolyte

PHOTOINDUCED SELF-STRUCTURED SURFACE PATTERNS ON FILMS OF EPOXY-BASED POLYMERS CONTAINING TRIFLUOROMETHYLSUBSTITUTED AZO CHROMOPHORES

SYNTHESIS OF A MAIN-CHAIN PHOTO-RESPONSIVE AZO POLYMER THROUGH AZO-COUPLING REACTION

FABRICATION OF PHOTORESPONSIVE ELECTROSTATIC MULTILAYERS CONTAINING DIAZONIUM-HYPERBRANCHED AZO POLYMER

Sequentially adsorbed electrostatic multilayers of branched side-chain polyelectrolytes bearing donor-acceptor type azo chromophores

Synthesis,self-assembly and photoresponsive properties of azobenzene-containing block copolymers