Abstract:(NiCuZn)Fe2O4 ferrite is a kind of soft magnetic material widely used in multilayer chip inductors because of its high resistivity and excellent magnetic properties at high frequencies. In this study, (Ni0.4Cu0.2Zn0.4)Fe2O4 ferrite powder was prepared by ultrasonic-assisted chemical co-precipitation method, the effect of calcination temperature on the structure and properties of ferrite powders was investigated by modern analytical methods that include differential thermal analysis, X-ray diffraction, transmission electron microscopy, infrared spectroscopy, and vibrating sample magnetometer, respectively. The results show that the grain size increased from 23.5 nm to 38.6 nm and the lattice size increased from 8.384 Å to 8.390 Å with the increase of calcination temperature from 600°C to 900°C. The TEM shows that the powder particle was uniform and dispersible, and the particle size was about 30nm at 800°C calcination. The saturation magnetization of ferrite powder increases from 45.85emu/g to 50.65emu/g and the coercivity decreases from 65.50Oe to 46.23Oe with the increase of calcination temperature from 700°C to 900°C. The uniform and fine nano-crystalline ferrite particles would reduce the sintering temperature and improve the stability of the properties for spinel ferrite. The preparation of nano-spinel ferrite by ultrasonic-assisted co-precipitation is a worthy wet process for application.

The effect of additives on hydrothermal preparation of nanometer Mn, Zn ferrite particles

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles

Effects of Fe2+ Content in Raw Materials on Mn–Zn Ferrite Magnetic Properties

The effect of sintering conditions on thermal stability and magnetic properties of Ni0.4Zn0.2Mn0.4Fe2O4 ferrites

Preparation of Magnetic Nanoparticles for Hyperthermia and the Impact of Aggregation State on Heating Effect

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

Sintering test research with addition of hematite concentrate

Effects on Direct Synthesis of Large Scale Mono-Disperse Ni0.5zn0.5fe2o4 Nanosized Particles

Preparation and characterization of Mn-Zn ferrite nanoparticles for tumor hyperthermia

The Effect of the Calcination Time on the Microstructure and Properties of MnZn Ferrite Powders

Optimum Sintering Temperatures and Magnetic Properties of Mn-Zn Ferrites Doped with Y2O3

Preparation and Properties of Nanosize MnZn Ferrite from Δ-Feooh

Room Temperature Preparation of Nanocrystalline MnCuZn Ferrite Powder by Auto-Combustion of Nitrate-Citrate Gels

Effect of nanoparticles on the magnetic properties of Mn–Zn soft ferrite

The Effect of Particle Size of Nano NiZnCu Ferrite Powders on Sintering Behavior, Microstructure and Electromagnetic Properties

Preparation and Characterization of Mn-Zn Ferrite Magnetic Nanoparticles for Tumor Hyperthermia

Hydrothermal formation of Ni-Zn ferrite from heavy metal co-precipitates

Influence of Calcination Temperature on Microstructure and Properties of (NiCuZn)Fe2O4 Ferrite Prepared via Ultrasonic-Assisted Co-Precipitation

The Preparation and Haracterization of Nanograined soft Magnetic Mn-Zn Ferrite