Abstract:In this paper, the Ti-6Al-4V(TC4) alloy specimens pre-coated with Ti-Cu-Al multilayer films were plasma nitrided at different temperatures (673K-823K), and their microstructure and mechanical properties were studied. Surface hardness changes induced by pre-coating combined with plasma nitriding were also analyzed and correlated with microstructural features and elemental distribution. Ti-Cu-Al multilayer films with clear interfaces on deformed TC4 alloy were fabricated. The multilayer structure survived after nitriding, and a thick gradient nitrided layer with a gradient distribution of N elements was formed. The bonded nitride on the surface provides high hardness, reaching 948HV at 723K. In addition, the nitride TC4 alloy's wear resistance exhibits a significant improvement compared with the untreated specimen, especially at 823K, the mass wear rate decreased by more than 80%. It is mainly attributed to the N/metal element gradient distribution of the thick nitride layer. The nitriding behavior of α-Ti/Cu/Al was investigated by first-principles calculations. According to the thermodynamic calculation results, N atoms preferentially occupy the octahedral interstitial sites of α-Ti and the tetrahedral interstitial sites of Al. It is worth noting that N atoms have poor thermodynamic stability in Cu, which is consistent with the experimental results. The calculated elastic properties agree with the experimental cross-sectional hardness results, showing a smooth decreasing trend of the complex modulus and hardness on the micrometer length scale and explaining the improved structure performance. These results may provide crucial inspirations for future experimental work preparing high-performance nitrided layers.

Comparison of surface properties of Ti-6Al-4V coated with titanium nitride, TiN+TiC+Ti(C,N)/DLC, TiN/DLC and TiC/DLC films by plasma-based ion implantation

Tribological behavior of different films on Ti-6Al-4V alloy prepared by plasma-based ion implantation

Effect of the DLC coating on the surface properties of the NiTi alloys

Deposition of DLC coating on biomedical TiNi alloys by plasma based ion implantation to improve surface properties

Surface characteristics and corrosion behavior of DLC film on NiTi alloys

Ti-TiC-TiC/DLC gradient nano-composite film on a biomedical NiTi alloy.

Characterization of TiN, TiC and TiCN coatings on Ti–50.6 at.% Ni alloy deposited by PIII and deposition technique

Surface modification of NiTi alloys using diamond-like carbon (DLC) fabricated by plasma immersion ion implantation and deposition (PIIID)

Tribological Behavior of TiC/DLC Multilayers Prepared on Ti–6Al–4V Alloy by Plasma-Based Ion Implantation

Diamond-Like Carbon Thin Films Deposited On Ti6al4v Alloy Surface By Plasma Gun At Atmospheric Pressure

EFFECT OF C2H2 FLOW RATE ON THE DEPOSITION OF TI-TIC-TIC/DLC GRADIENT NANO-COMPOSITE FILM ON NITI ALLOY

DLC films fabricated by plasma immersion ion implantation and deposition on the NiTi alloys for improving their corrosion resistance and biocompatibility

Mechanical and Corrosion Study of Diamond-Like Carbon Coating on Niti Alloys

Surface Characteristics and Electrochemical Corrosion Behavior of NiTi Coated with Diamond-Like Carbon

The corrosion behavior and hemocompatibility of TiNi alloys coated with DLC by plasma based ion implantation

Tribological Properties of Plasma Source Ion Implanted DLC Film on 2024 Aluminum Alloy

Modification mechanism of Ti-6Al-4V alloy with pre-coated Ti-Cu-Al multilayer film treated by ion nitriding: Experiments and first-principles calculations

Mechanical Properties of Ti(C(0.7)N(0.3)) Film Produced by Plasma Electrolytic Carbonitriding of Ti6al4v Alloy

Structure and Frictional Characteristics of Ti–6Al–4V Plasma-Based Ion Implanted with Nitrogen then Acetylene

(AlCrNbSiTi)N/TiN multilayer films designed by a hybrid coating system combining high-power impulse magnetron sputtering and cathode arc deposition

Tribological Behaviour of Duplex Treated Ti–6Al–4V: Combining Nitrogen PSII with a DLC Coating