Abstract:A series of Si3N4/BAS compositions of 20, 40, 60, 80 and 100 wt.% barium aluminosilicate (BAS) were hot-pressed at relatively low sintering temperature (1450 °) for a 30–60 min soak at a pressure of 10–20 MPa under N2 atmosphere. Elongated rod-like β-Si3N4 whiskers were formed for compositions with 20–80 wt.% BAS. No metal ions were dissolved in Si3N4 crystal lattices. The microstructure varied with composition. The relative content of rod-like β-Si3N4 whiskers increased with increasing BAS content. Densities of all the specimens with BAS contents more than 20 wt.% were >99% of the theoretical density. With a 30 min soak, the room temperature (RT) flexural strength increased from 259.1 to 323.0 MPa from 20 to 40 wt.% BAS and then decreased to 70.6 MPa for 100 wt.% BAS. The fracture toughness increased from 2.40 to 3.24 MPa m1/2 from 20 to 60 wt.% BAS and then decreased to 1.78 MPa m1/2 for 100 wt.% BAS. With a 60 min soak, the RT flexural strength of 40 wt.% BAS without monoclinic BAS seeds was 379.6 MPa and retained 87.9, 93.8 and 94.2% of their RT values at 1000, 1100 and 1200 °C, respectively; in contrast, the RT flexural strength of 40 wt% BAS containing 8 wt% BAS seeds was 519.4 MPa and retained 87.3, 63.0 and 51.9% of their RT values at 1000, 1100 and 1200 °C, respectively. Monoclinic BAS seeds had little effect in accelerating the hexagonal→monoclinic phase transformation of BAS glass ceramics.

Preparation and Characterization of BAS Reinforced with SiC Platelets

Microstructure and mechanical properties of SiC platelet reinforced BaOAl2O32SiO2 (BAS) composites

Mechanical Property and Microstructure of SiC Platelets (SiCpl) Reinforced BAS Matrix Composites

Fabrication and Characterization of Barium Aluminum Silicate-Silicon Nitride Composites

Preparation and Mechanical Properties of C_(sf)/BAS Glass Ceramic Matrix Composites

Microstructure and Mechanical Properties of Sicw/Bas Glass-Ceramic Composites

Microstructure and mechanical properties of barium aluminosilicate glass-ceramic matrix composites reinforced with SiC whiskers

Synthesis and Microstructure Evolution of Β‐sialon Fibers/barium Aluminosilicate (BAS) Glass‐ceramic Matrix Composite with Enhanced Mechanical Properties

Low temperature hot-pressed BAS matrix composites reinforced with in situ grown Si3N4 whiskers

Fracture Behavior of SiC-Whisker-Reinforced Barium Aluminosilicate Glass-Ceramic Matrix Composites

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Hot-press sintering studies of sol-gel-prepared composite powders: A novel preparation method to improve mechanical properties of BN-BAS composite ceramics

Microstructure and Property Enhancement of Silicon Nitride-Barium Aluminum Silicate Composites with Β-Si3n4 Seed Addition

Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets

Microstructure and Mechanical Properties of Y-SiAlON/BaSi2Al2O8 Composite Ceramics

Microstructure and Mechanical Properties of SiC Platelet Reinforced (α + Β) Sialon Ceramic Composites

Microstructure compatibility and its effect on the mechanical properties of the α-SiC/β-Si3N4 co-reinforced barium aluminosilicate glass ceramic matrix composites

Preparation and Mechanical Properties of Carbon Nanotubes Reinforced Barium Aluminosilicate-Silicon Nitride Composites

Mechanical Properties and Toughening Mechanisms of Si3n4 Matrix Laminated Ceramic Composite

Microstructure, properties and mechanisms of reinforcing for C-f/SiO2 ceramic matrix composite

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing