Abstract:A potentially manufacturable liquid‐source MOCVD process was applied to deposit platinum (Pt) films (12–140 nm) on thermally oxidized Si substrates. The deposition of Pt films was carried out at a substrate temperature of 350 °C by oxygen‐assisted pyrolysis of complex precursors in a low‐pressure, hot‐wall reactor. The effects of two different metal–organic precursors, a) trimethyl methyl cyclopentadienyl platinum [(CH3)3CH3CpPt], and b) platinum acetylacetonate [Pt(acac)2], on the properties of Pt films were studied. Although the polycrystalline Pt films deposited from Pt(acac)2 exhibited a preferred (111) orientation with a X‐ray intensity ratio of I(111)/I(200) = 40, the films deposited from (CH3)3CH3CpPt were highly (111) oriented with I(111)/I(200) = 270. The following properties were typical of Pt films from Pt(acac)2 as compared to Pt films from (CH3)3CH3CpPt: finer grain size (25 nm vs. 50 nm), smaller root mean square (rms) surface roughness (5 nm vs. 15 nm), and better step coverage (95 % vs. 35 %). These experimental findings indicated that growth of Pt films from Pt(acac)2 occurred under the kinetically‐limited regime, whereas the deposition of Pt from (CH3)3CH3CpPt was limited by the mass transport rate. Additionally, the temperature (4.2–293 K) dependence of the electrical resistivities (ρ) of Pt films was measured and the electron mean free paths were estimated. It was observed that ρ(T) deviated from Matthiessen's rule. Platinum thin films are grown on thermal‐SiO2/Si at 350 °C from (CH3)3‐CH3CpPt and Pt(acac)2. Films deposited from the first precursor show an orientation ratio of [I(111)/I(200) = 270], a large grain size of 50 nm, and poor conformality of 35–45 %, while those produced from Pt(acac)2 show [I(111)/I(200) = 40], finer grain structure, and excellent conformality of 85–95 % (see Figure). Film resistivity exhibits values of 23.6 and 27.6 μΩ cm.

Synthesis and Characterization of Optical Transmissive, Electrically Conductive Platinum and Platinum Oxide Semiconductor Thin Films

Gas Phase Fabrication of Morphology-Controlled ITO Nanoparticles and Their Assembled Conductive Films.

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Formation of Pb0.6sr0.4(Ti0.97mg0.03)O-2.97 Thin Films on Assembled Bottom Electrodes with Titanium Silicide Nanowires

Electrophoretic Deposition and Photoluminescent Properties of Eu-doped BaTiO3thin Film from a Suspension of Monodispersed Nanocrystallites

Formation of Silver Nano Particles in Percolative Ag‐PbTiO 3 Composite Dielectric Thin Film

Preparation and Photoluminescence of Nanocrystalline Si-Rich Silicon Oxide Films by Pecvd

MOCVD of Platinum Films from (CH3)3CH3CpPt and Pt(acac)2: Nanostructure, Conformality, and Electrical Resistivity

Hydrothermal Preparation and Characterization of Nanocrystalline Porous Tin Dioxide Thin Films

A Crucial Step to Platinum Nanocrystals with Special Surfaces: Control of Aquo/Chloro Ligand Exchange in Aqueous Ptcl62- Solution

Enhancement in Photoluminescence of Pt/Ag-Pt Embedded ZrO2 Thin Films by Plasma Co-sputtering

Thermal Wetting of Platinum Nanocrystals on Silica Surface

Preparation And Characterization Of Novel Nanoscopic Titanium Dioxide Phthalocyanine Complex Films

Preparation of colloidal solutions of thin platinum nanowires

Synthesis and Characterization of Nanoporous SnO2 Thin Film

Synthesis and Assembly of Catalytically Active Platinum-Doped Polymer Nanocomposites at the Liquid/liquid Interface

Investigation of structural and photoluminescence properties of nanocrystalline tin oxide thin films grown by ultrasonic spray pyrolysis method

Thermal Stability and Crystallization Processes of Pd78Au4Si18 Thin Films Visualized via In Situ TEM

Preparation and characterization of ultrafine neodymium oxide/TiO2/ORMOSIL sol-gel composite thin film

Synthesis and characterisation of thin-film platinum disulfide and platinum sulfide

Synthesis and Optical Properties of Metal Nanoparticles Embedded in Porous Anodic Alumina Oxide