Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Preparation of Active Carbon with High Specific Surface Area from Rice Husks

PREPARATION OF ACTIVATED CARBON WITH HIGH SPECIFIC SURFACE AREA FROM CORN COB

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

Facile, Low-Cost, and Sustainable Preparation of Hierarchical Porous Carbons from Ion Exchange Resin: an Improved Potassium Activation Strategy

Pine Sawdust Derived Ultra-High Specific Surface Area Activated Carbon: Towards High-Performance Hydrogen Storage and Supercapacitors

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Preparation of high specific surface area activated carbon from walnut shells by microwave-induced KOH activation

Preparation of High-Surface-Area Activated Carbon from Coconut Shell Fibers

Process Effects on Activated Carbon with Large Specific Surface Area from Corn Cob.

Preparation of Phosphate-activated Carbon from the Coconut Fibers

Preparation of Nanoporous Carbon from Rice Husk with Improved Textural Characteristics for Hydrogen Sorption

Orthogonal experimental study on activated carbon from biomass hydrolysis residues activated by carbon dioxide

Study of the Enhancements of Porous Structures of Activated Carbons Produced from Durian Husk Wastes

Effect of Two-Stage Process on the Preparation and Characterization of Porous Carbon Composite from Rice Husk by Phosphoric Acid Activation

Preparation and Performance Analysis of New Multi stage Porous Carbon Materials for Air Pollution Treatmentials on Atmospheric Pollution Sources under the Background of Carbon Peak and Carbon Neutrality

Synthesis and evaluation of activated carbon from rice husks for removal of humic acid from water

Preparation of Activated Carbon from Co-Pyrolysis Activation of Fly Ash and Biomass

Preparation of High Specific Surface Area and High Adsorptive Activated Carbon by KOH Activation

Preparation of High Surface Area Activated Carbon from Spent Phenolic Resin by Microwave Heating and KOH Activation

Designing microporous activated carbons from biomass for carbon dioxide adsorption at ambient temperature. A comparison between bagasse and rice by-products