The photoelectrochemistry of transition metal-ion-doped TiO2 nanocrystalline electrodes and higher solar cell conversion efficiency based on Zn2+-doped TiO2 electrode

Yanqin Wang,Yanzhong Hao,Humin Cheng,Jiming Ma,Bin Xu,Weihua Li,Shengmin Cai

DOI: https://doi.org/10.1023/A:1004658629133

IF: 4.5

1999-01-01

Journal of Materials Science

Abstract:Metal-ion-doped TiO 2 nanoparticles were prepared with hydrothermal method. The change of photocurrents at different electrode potentials and wavelengths of incident light showed two different characteristics for various transition metal-ion-doped TiO 2 electrodes. In Zn 2+ and Cd 2+ -doped TiO 2 electrodes, a characteristic of n-type semiconductor was observed and the incident photon to conversion efficiency (IPCE) were larger than that of pure TiO 2 electrode at the thickness of electrode film of 0.5 μm when the content of doped metal ion was less than 0.5%. The effect of the thickness of films on IPCE was also investigated. The IPCE of pure TiO 2 electrode was strongly dependent on the thickness of films. The change tendency of the IPCE for Zn 2+ -doped TiO 2 (0.5% Zn 2+ ) electrodes with its thickness was different from that of pure TiO 2 . In Fe 3+ , Co 2+ , Ni 2+ , Cr 3+ and V 5+ -doped TiO 2 electrodes, a phenomenon of p-n conversion was observed. The difference of photoresponse and the value of photocurrents are dependent on the doping method and concentration of the doped metal ions. The maximum conversion efficiency of RuL 2 (SCN) 2 -sensitized Zn 2+ -doped TiO 2 solar cell (1.01%) was larger than that of RuL 2 (SCN) 2 -sensitized pure TiO 2 solar cell (0.82%) at the same conditions when 0.5 mol · l −1 (CH 3 ) 4 N · I + 0.05 mol · l −1 I 2 in propylene carbonate solution was used as electrolyte.