Abstract:We report multicolor upconversion emissions including the blue-violet, green, and red lights in a Tm3+/Er3+ codoped tellurite glass photonic microwire between two silica fiber tapers. A silica fiber is tapered until its evanescent field is exposed and then angled-cleaved at the tapered center to divide the tapered fibers into two parts. A tellurite glass is melted by a gas flame to cluster into a sphere at the tip of one tapered fiber. The other angled-cleaved tapered fiber is blended into the melted tellurite glass. When the tellurite glass is melted, the two silica fiber tapers are simultaneously moving outwards to draw the tellurite glass into a microwire in between. The advantage of angled-cleaving on fiber tapers is to avoid cavity resonances in high index photonic microwire. Thus, the broadband white light can be transmitted between silica fibers and a special optical property like high intensity upconversion emission can be achieved. A cw 1064 nm Nd:YAG laser light is launched into the Tm3+/Er3+ codoped tellurite microwire through a silica fiber taper to generate the multicolor upconversion emissions, including the blue-violet, green, and red lights, simultaneously. (C) 2010 Optical Society of America

Frequency upconversion in homemade Tm3+-doped silica fibers pumped by 1053 nm

Multicolor upconversion emissions in Tm 3+/Er3+ codoped tellurite photonic microwire between silica fiber tapers.

Frequency upconversion in TM3+-doped silica fibers in the visible region

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Visible and near infra-red up-conversion in Tm3+/Yb3+ co-doped silica fibres under 980 nm excitation

Upconversion in Highly Doped Er~(3+)-Yb~( 3+) Fiber Pumped by Ti∶Sapphire Laser at 800 nm

On the laser frequency upconversion from 1313nm to 780nm in the Er3+-doped and Er3+/Yb3+-doped germanosilicate single-mode optical fibers

Efficient blue upconversion emission due to confined radiative energy transfer in Tm3+–Nd3+ co-doped Ta2O5 waveguides under infrared-laser excitation

Infrared -to-visible upconversion emissions in Er3+ doped TeO2-based oxyhalide glasses

Cooperative Energy Transfer Frequency Upconversion in Tb3+/Yb3+-codoped Oxyfluoride Glasses

Enhanced 1.8 Μm Emission in Cr3+/Tm3+ Co-Doped Fluorogermanate Glasses for a Multi-Wavelength Pumped Near-Infrared Lasers

Infrared-to-Visible Upconversion Emissions in Er3+ Doped TeO2-Based Oxyhalide Glasses

Upconversion of 1.064 Μm Nd:YAG Laser Pulses into Intense Visible Light in Erbium-Doped Phosphate Fibers

The Upconversion Phenomenon in Tm3+-Doped Tellurite Glass

Infrared-to-Visible Upconversion Emissions in Er<sup>3+</sup> Doped TeO<sub>2</sub>-Based Oxyhalide Glasses

Generation of the 1.871 μm laser oscillation from a monomode Tm3+-doped silicate fiber

Fluorescence Emission Centres and the Corresponding Infrared Fluorescence Saturation in a Bismuth-Doped Silica Fibre

Enhanced 1.8 μm emission in Er3+/Tm3+ co-doped lead silicate glasses under different excitations for near infrared laser

Upconversion Emissions from High Energy Levels of Tb3+ under Near-Infrared Laser Excitation at 976 Nm

Nd-Doped Glass Fiber Lasers And Up-Conversion Lasers

An Efficient 1.8 Μm Emission in Tm3 + and Yb3 +/tm3 + Doped Fluoride Modified Germanate Glasses for a Diode-Pump Mid-Infrared Laser