Abstract:The systems of CrO3/SiO2 and CrO3/gamma-Al2O3 have been studied by X ray diffraction (XRD). The CrO3/SiO2 (or CrO3/gamma-Al2O3) samples with various amounts of CrO3 were prepared by mixing CrO3 and SiO2 (or gamma-Al2O3) in dry atmosphere, and by calcining at temperatures below the melting point of CrO3 (196 degrees C) for 24 hrs. In order to protect the samples front moisture in the XRD measurement, a special sample holder (see Fig. 1]) was used. The maximum dispersion amounts (dispersion threshold)of CrO3 on SiO2 at various temperatures(101 to 170 degrees C) have been obtained from the XRD quantitative phase analysis (see Fig.3). It has been shown that the dispersion thresholds change with calcination temperatures. For CrO3/SiO2 system, as temperature changes from 101 to 170 degrees C, the threshold increases from 0.27 to 0.38 g CrO3/g SiO2 (see Fig.4). For CrO3/gamma-Al2O3 system, as temperature changes from 120 to 171 degrees C, the threshold changes from 0.22 to 0.42 g CrO3/g gamma-Al2O3 (see Fig.5). The specific surfaces of the SiO2 and gamma-Al2O3 are 364 and 178 m(2)/g. In terms of unit surface area, the dispersion thresholds for CrO3 on SiO2 and for CrO3 on gamma-Al2O3 at 150 degrees C are 0.096 and 0.191 g CrO3/100m(2) respectively, According to a closepacked monolityer model, the monolayer capacity of CrO3 on a support should be 0.081 g CrO3/100m(2). The experimental results indicate that CrO3 dispersed on SiO2 or gamma-Al2O3 are not monolayers. They are quite different from those systems we reported before. In those systems the active components could disperse spontaneously onto the carrier surface to form a monolayer or submonolayer and have definitive dispersioe thresholds. The dispersion thresholds of CrO3 on SiO2 or gamma-Al2O(3) increases with calcination temperature, and can exceed their monolayer capacities.These behaviours can be attributed to the polymerization of CrO3. We suggested that heating at a lower temperature CrO3 reacted with SiO2 to form surface compound and heating at a higher temperature CrO3 formed homopoly-acid-radical.

Diapersion of Sucrose on the Surface of Alumina

Different Dispersion Behavior of Glucose and Sucrose on Alumina and Silica Surfaces

Investigation on Synthesis Conditions of Ni-CaO/Al2O3 Sorption Complex Catalyst by Hydrothermal Precipitation Method

Sucrose-Assisted Preparation of High Surface Area Γ-Alumina and Influence of Sucrose Content on Its Textural Properties

Preparation of High-Surface-Area Γ-Alumina by Assistance of Sucrose

Surface Energy Study Of Alooh Coated Calcium Carbonate By Inverse Gas Chromatography

Spontaneous Monolayer Dispersion of Some Organic Compounds on Oxide-supports

Uniform carbon-covered alumina synthesized by pyrolysis of sucrose/γ-Al2O3

Uniform carbon-covered alumina synthesized by pyrolysis of sucrose/gamma-Al2O3

Surface Hydroxyl-Determined Migration and Anchoring of Silver on Alumina in Oxidative Redispersion

Adsorption and Porosity Properties of Carbon-Covered Alumina Surfaces

The Morphologically Controlled Synthesis and Application of Mesoporous Alumina Spheres

Applications of Monolayer-Dispersed Organic Compounds in the Preparation of Related Materials

A Fractal Study on the Dspersing Processes on the Surface

APPLICATION OF XPS TO STUDYING DISPERSION AND SURFACE STATE FOR MoO 3 SUPPORTED ON THE SURFACE OF TiO 2 , Γ-Al 2 O 3 AND SiO 2

Measurement of Dispersion Capacity of Moo3 on Low Specific Surface Support Alpha-Al2o3

Dispersed State of Cro3 on the Surface of Gamma-Al2o3 or Sio2

Surface Alumina Species on Modified Titanium Dioxide: A Solid-State 27al MAS and 3QMAS NMR Investigation of Catalyst Supports

Spontaneous Monolayer Dispersion of Oxides and Salts onto Surfaces of Supports: Applications to Heterogeneous Catalysis

Dispersion behavior and stabilization mechanism of alumina powders in silica sol