Study on Dispersion Speed and Mechanism of MoO3 and CuCl on the Surface of Γ-Al2o3
Xu Xianping,Xie Youchang,Zhao Biying,Tang Youqi
DOI: https://doi.org/10.3866/pku.whxb19900303
1990-01-01
Acta Physico-Chimica Sinica
Abstract:It has been shown that many oxides and salts can disperse spontaneously onto supports with large surfacc area ([1]). A typical example studied widely is the dispersion of MoO3 on gamma-Al2O3. However, the research work about the dispersion mechanism and kinetics is quite few.Knozinger etc, ([2]) suggested that the dispersion of MoO3, onto the surface of gamma-Al2O3 may occur through a "gas phase transport" mechanism mainly by assuming an intermediate MoO2(OH)(2),(g), and the presence of water is necessary. Their conclusion was based on a fact that after heating a mixture of MoO3 and gamma-Al2O3 in the presence of H2O vapour at 450(degrees)C, the characteristic peak at of monolayer dispersed MoO4 in Lacer Kaman Spectrum (in situ) appears, but after heating the mixture in dry oxygen, it can not be observed. However, before long they discovered by ISS that MoO3 concentration on the surface of 7-Al2O3 (indicated by I Mol(A1)) raised with heating time even if the mixture is heated in dry oxygen. So they revised their opinion and suggested that in the absence of water MoO2 couldn't disperse as a monolayer phase, but could spread on the surface of gamma-Al2O3 ([3].)We have suggested that the dispersion of oxides or salts onto apports as a monolayer or submonolayer occurs through their surface diffusion. An XRD in situ study on the disperson kinetics of MoO3 or 7-Al2O3 by Yang Hengsei i, ([4]) supported the surface diffusion mechanism.The objective of this work has been to study the effect of water on the dispersion rates of MoO3 and CuCl on gamma-Al2O3 and discuss the disperson mechanism.(1) MoO3 7-Al2O3 systemA physical mixture of MoO3 and 7-Al2O3 (surface area 233 m(2) center dot g(-1)) at a ration of 1:10 by weight was prepared by tumbling and gringding in an agale molar. Then the mixture was pressed into a stainless steel sample holder, and heated in a certain gas flow of about 60 ml center dot min(-1). At first, the sample was heated at 200 degrees C for an hour in order to remove the water in the sample, then heated to a certain temperature and held it (+/- 1 degrees C). The XRD peak (040) of MoO3 was scammed repeaily to get the peak area as a function of heating time. Fig.1 shows the relationship between the amount of crystalline MoO3 obtained from the peak area and the heating time at 450 degrees C in dry oxygen or in oxygen with H2O vapour. It can be seen that MoO3 can disperse in dry oxygen, but its disperson rate is slow. The disperson process can be speed up greatly in the presence of H2O vapour. The results obtained in a N-2 flow are similar to those obtained in an O-2 flow.The dispersion rates at 500 degrees C are much faster than those at 450 degrees C either in dry O-2 or in dry N-2,N- and the presence of water vapour can promote the disperson process too, as shown in Fig.2.Fig.3 shows that heating temperature can exert a tremendous influence on the disperson rate, and 550 degrees C the disperson process can complete within 7 hours even if in dry oxygen.These results indicate that the key factor for MoO2 disperson is the temperature high enough, and the presence of water vapour only speeds up the disperson process.That in dry O-2 pr M-2 the characterisitic peak at 950 cm(-1) didn't appear in the in situ Raman Spectra might be attributed to the following reasons.(a) Steneel etc. ([5]) reported that the structure of the surface molybdate species is changeable with the amount of supported MoO2 and the water cotent of the samples. The Mo-O stretching vibration is at about iCO(2) cm(-1) in dry samples, whereas in H2O-exposed simples the frequency is near 350cm(-1.) The reason is the bond order and the bond length of MO=O in molybdeum-oxygen compounds are related with their degree of hydratien (i.e. hydrexylation).For verifing this point, a supplymental experiment has been done. The results are shown in Fig.4. Obviously, in this case there is a monolayer phase Mo on the surface of gamma-Al2O3, but if the sample is dried, the charateristic peak at 950 cm(-1) can not be observed yet. (b) The Raman scatter across section of the characterisitic peak of the monolayer disperson phase is only about 1/40 of that of crystalline MoO3 and the shape of the peak is broad. Therefore, it is difficult to detect the peak of the monolayer disperson phase if there is much crystalline MoO3 in the sample.We consider that the dispersion of MoO3, occurs through a surface diffusion mechanism. The kinetic driving force of diffusion is a concentration gradient of MoO3, on a surface, but the diffusion resistance depends on the surface property of a support. The hydration (i.e,hydrexylation) of the surface of gamma-Al2O3 makes the active energy of surface diffusion lower, and favours mobiling of MoO3, on the surface, and consequently the rate of dispersion increases, The mechanism might be below:[GRAPHICS](2) CuCl/gamma-Al2O3 systemCuCl can be dispersed on the surface of gamma-AlO3 to form an adsorbent for CO or ethylene. Since CuCl is hydrophobic, it can be expected that the presence of water on the surface of a support will resist disperson of CuCl. An in situ XRD study on a physical mixture of CuCl and gamma-Al2O3 (1:10 by weight) approves this point.Fig. 5 gives the amount of crystalline CuCl in the mixture as a function of heating time at 280 degrees C in dry nitrogen or in nitrogen with water vapour. It can be seen that CuCl can disperse easily either in the presence of water vapour or absence of water vapour. However, in contract to MoO3-gamma-Al3O3 system, the presence water obstructs the dispersion of CuCl on the surface of gamma-Al2O3 to some extent.The dispersion of FeCl2 on the surface of gamma-Al2O3 has also been studied. The experiment has to be done under an absolute no-water condition because FeCl3 is hydrolyzed very easily. The results of XRD and Mossbauer Spectra([7]) have shown that FeCl3 can be dispersed on gamma-Al2O3 as a monolayer at 180 degrees C in dry nitogen.In conclusion, the dispersion of an oxide or salt onto the suface of a support can occur through a surface diffusion mechanism if only the temperature is high enough. For different systems the presence of water vapour may have a different influence upon their disperson rates.