Abstract:In this study, a crack-free pyrolysis process of partially cured precursor powder compacts was developed to prepare dense silicon boron carbonitride (SiBCN) monoliths at much lower temperatures (1300 degrees C), thereby circumventing the challenges of sintering densification (> 1800 degrees C). Unlike the elastic fracture in over-cured precursors or the viscoelastic deformation in under-cured precursors, the partially cured precursor, exhibiting elastic-plastic deformation behavior, facilitates limited nanoscale pore formation in a dense structure, achieving a balance between crack-free pyrolysis and densification. Compared to SiBCN derived from the over-cured precursor (sigma = similar to 159 MPa, K-IC = 1.9 MPa center dot m(1/2), Vickers hardness (HV) = 7.8 GPa, and E = 122 GPa), the resulting SiBCN monolith exhibited significantly improved mechanical properties (sigma = similar to 304 MPa, K-IC = 3.7 MPa center dot m(1/2), HV = 10.6 GPa, and E = 161 GPa) and oxidation resistance. In addition, this study investigated the high-temperature performance of SiBCN monoliths, including crystallization and oxidation, and determined the oxidation kinetics induced by pore structure healing and the different oxidation mechanisms of Si-C-N and B-C-N clusters in the amorphous structure. Due to its unique composition and structure, the SiBCN ceramic oxide layer exhibits exceptional self-healing effects on repairing the nanoporous system in the initial stage and shows outstanding high-temperature stability during prolonged oxidation, mitigating adverse effects from bubble formation and crystallization. Due to the nanoporous structure, the oxidation rate is initially controlled by gas diffusion following a linear law before transitioning to oxide layer diffusion characterized by a parabolic law. Finally, due to different valence bond configurations, Si-C-N transforms into an amorphous SiCNO structure after phase separation, unlike the nucleation and growth of residual B-N-C.

A NEW WAY OF MAKING BUCKY ONION BY THERMAL DECOMPOSITION OF SiC NANOMETER POWDERS UNDER HIGH-TEMPERATURE AND VACUUM

GROWING CARBON BUCKONIONS BY RADIO FREQUENCY PLASMA-ENHANCED CHEMICAL VAPOR DEPOSITION

Investigation on the Structure and Electric Properties of Bucky Onions

In Situ Formation and Structure Tailoring of Carbon Onions by High-Resolution Transmission Electron Microscopy

Properties of Carbon Onions Produced by an Arc Discharge in Water

Small onion-like BN leads to ultrafine-twinned cubic BN

Sulfur‐Assisted Approach for the Low‐Temperature Synthesis of Β‐sic Nanowires

Synthesis of Carbon 'onions' in Water

Synthesis and Structure of Graphitic Buckybundles

A practical method for the production of hollow carbon onion particles

Fabrication and characterization of amorphous SiBCN powders

Microstructure and thermal stabilities in various atmospheres of SiB0.5C1.5N0.5 nano-sized powders fabricated by mechanical alloying technique

Ultrahard Nanotwinned Cubic Boron Nitride.

Fabrication of Dense SiBCN Monolith at a Lower Temperature Andits High-Temperature Performance

A sector deposition mechanism of carbon onions operated in a large discharge furnace

Is There a Stable Bucky-diamond Structure for SiC Clusters?

Carbon content-dependent microstructures, surface characteristics and thermal stability of mechanical alloying derived SiBCN powders

High-Yield Synthesis of SiC@SiO2 Core-Shell Nanowires on Graphite Substrates for Energy Applications

Ultrahigh vacuum scanning probe microscopy studies of carbon onions

Boron‐dependent Microstructural Evolution, Thermal Stability, and Crystallization of Mechanical Alloying Derived SiBCN

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction