Abstract:Structure and morphology development during the isothermal crystallization and subsequent melting of syndiotactic polypropylene (sPP) was studied with differential scanning calorimetry (I)SQ, time-resolved simultaneous small-angle X-ray scattering (SAXS), and wide-angle X-ray diffraction (WAXD) methods with synchrotron radiation. The morphology of sPP isothermally crystallized at 100 degreesC for 3 h was also characterized with transmission electron microscopy (TEM). Time- and temperature-dependent parameters such as the long period (L), crystal lamellar thickness (l(c)), amorphous layer thickness (l(a)), scattering invariant (Q), crystallinity (X-c), lateral crystal sizes (L-200 and L-010), and unit cell dimensions (a and b) were extracted from the SAXS and WAXD data. Results indicate that the decreases in L and lo with time are probably due to the formation of thinner crystal lamellae, and the decreases in a and b are due to crystal perfection. The changes in the morphological parameters (Q, X-c, L, and l(c)) during subsequent melting exhibited a two-stage process that was consistent with the multiple melting peaks observed in DSC. The two high-temperature peaks can be attributed to the melting of primary lamellae (at lower temperatures) and recrystallized lamellae (at higher temperatures), An additional minor peak, located at the lowest temperature, was also visible and was related to the melting of thin and defective secondary lamellae. TEM results are consistent with the SAXS data, which supports the assignment of the larger value (l(1)) from the correlation function analysis as l(c). WAXD showed that the thermal expansion was greater along the b axis than the a axis during melting. (C) 2001 John Wiley & Sons, Inc.*.

Temperature Rising Elution Fractionation of Syndiotactic Polypropylene Prepared by Homogeneous and Supported Metallocene Catalysts

Nonisothermal Crystallization of S-Pp Fractions

Particle morphology of syndiotactic polystyrene prepared with homogeneous metallocene catalyst

STUDIES ON BULK SYNDIOTACTIC POLYMERIZATION OF STYRENE CATALYZED BY METALLOCENE

Influence of Syndiotacticity and Annealing Temperature on the Double Melting Peak Behaviour of Syndiotactic Polypropylene

Full‐range Kinetic Study on Bulk Syndiotactic Polymerization of Styrene with Homogeneous Metallocene Catalysis

Temperature rising elution fractionation of polypropylene produced by heterogeneous Ziegler-Natta catalysts

Characterization of isotactic polypropylene prepared with dimethylsilyl bis(1-indenyl)zirconium dichloride supported on methylaluminoxane pretreated silica

Microtacticity of Polypropylene Fractions Produced by Different Active Sites of Heterogeneous Ziegler-Natta Catalyst

Temperature Rising Elution Fractionation of Polypropylenes Produced by Heterogeneous Ziegler-Natta Catalysts Containing Different Internal Donors

Characterization of Intramolecular Composition Heterogeneity of Metallocene-Based and Conventional Ethylene-Butene Copolymers Using Tref/Dsc

Characterization of Microstructure of Polypropylene Alloys

Application of Temperature Rising Elution Fractionation in Polyolefins

Temperature rising elution fractionation of PP/PE alloy and thermal behavior of the fractions

Separation and identification of ethylene-propylene block copolymer

Crystallization Behavior of Syndiotactic Polypropylene: Effect of Solvent of Varying Molecular Size

Influence of electron donors on the tacticity and the composition distribution of propylene-butene copolymers produced by supported Ziegler-Natta catalysts

COMPOSITION AND TACTICITY DISTRIBUTION OF PROPYLENE BUTENE COPOLYMER

Synthesis Of Powdery Syndiotactic Polystyrene With Homogeneous Metallocene Catalysts - Kinetics And Morphologies

Structure and morphology development in syndiotactic polypropylene during isothermal crystallization and subsequent melting

Blends of Syndiotactic Polystyrene and Isotactic Polypropene Prepared Using a Ziegler‐Natta Catalyst Containing a Novel Donor