Origin of coercivity in an anisotropic Sm(Fe,Ti,V)12-based sintered magnet
Xin Tang,H. Sepehri-Amin,T. Ohkubo,K. Hono,J. S. Zhang,A. K. Srinithi
DOI: https://doi.org/10.1016/j.actamat.2021.117161
IF: 9.4
2021-09-01
Acta Materialia
Abstract:<p>We have demonstrated an anisotropic bulk SmFe<sub>12</sub>-based sintered magnet with sufficiently large coercivity of <em>μ</em><sub>0</sub><em>H</em><sub>c</sub>=1.0 T and a remanence ratio (<em>M</em><sub>r</sub>/<em>M</em><sub>s</sub>) of 0.84 using conventional liquid sintering process of nitrogen jet-milled powders with the nominal composition of Sm<sub>8</sub>Fe<sub>73.5</sub>Ti<sub>8</sub>V<sub>8</sub>Ga<sub>0.5</sub>Al<sub>2</sub> (at.%). The moderate saturation magnetization of <em>μ</em><sub>0</sub><em>M</em><sub>s</sub> =0.74 T is due to the dissolution of a large amount of stabilizing elements, Ti, V, and Al, in the 1:12 phase. The anisotropy field of the main 1:12 phase was determined to be µ<sub>0</sub><em>H</em><sub>A</sub>=10.2 T. Detailed multi-scale microstructure characterizations by scanning electron microscope (SEM) and scanning transmission electron microscope (STEM) showed the magnet consists of Sm(Fe,Ti,V,Al)<sub>12</sub> grains with the ThMn<sub>12</sub>-type crystal structure with a size distribution of ∼3−15µm that are enveloped by ∼3 nm thick Sm-rich amorphous intergranular phase. Secondary phases including metallic (Sm,Ga)-rich, SmO<sub>x</sub>, and Fe<sub>2</sub>(Ti,V) phases coexist with the 1:12 phase. Measured angular dependence of coercivity follows Kondorsky type magnetization reversal, suggesting the coercivity arises due to the pining of magnetic domain walls. Magneto-optical Kerr effect (MOKE) microscopy revealed magnetization reversal starts at the grain boundaries and interphase interfaces and thin amorphous intergranular phases act as the pinning sites against magnetic domain wall propagation. Small micromagnetic parameter <em>α</em>∼0.164 estimated by fitting to the Kronmüllar equation suggest that the reduction of the grain size and engineering of the intergranular phase to an Fe-lean composition are necessary to improve the coercivity toward µ<sub>0</sub><em>H</em><sub>A</sub>/3=3.4 T. This work provides guidelines on an optimum microstructure to develop an anisotropic bulk SmFe<sub>12</sub>-based sintered magnet with a sufficiently large coercivity.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering