Abstract:TiB 2 /Al 3 Ti/Al 2 O 3 composite nano-powder has been prepared by sintering TiO 2 , Al powder, and B 2 O 3 with molten salt as the medium. The sintered powder was characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy–energy dispersive spectroscopy (TEM–EDS), and x-ray photoelectron spectroscopy (XPS). The results illustrated the successful synthesis of TiB 2 /Al 3 Ti/Al 2 O 3 nano-powder when the mass ratio of molten salt to reactants was 3 after calcination at 1000°C for 3 h. The synthesized powder comprises baseball-like, lamellar, and spheroidal nanoparticles, with TiB 2 and Al 2 O 3 presenting a nano-scale mosaic structure which was used to reinforce aluminum-based composites. The synthesis mechanism of TiB 2 /Al 3 Ti/Al 2 O 3 nano-powder was also investigated. With the increase in temperature, Al 2 O 3 , Al 3 Ti, and Al 8 B 2 O 15 intermediate phases were first generated. Then, the further increase in temperature promoted the dissolution and diffusion of the unstable Al 8 B 2 O 15 phase in the molten salt, increasing the contact between Ti and B, thus producing the TiB 2 phase. By adding the TiB 2 /Al 3 Ti/Al 2 O 3 powder to the A6061 aluminum alloy at a 5% mass fraction, the Vickers hardness of the original alloy increased by 55.30%.

In-Situ Preparation of Al/Tial3(P) Composite by Direct Reaction Between Molten Al and Tio2 Powder

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

Microstructure and properties of in-situ reaction Al/Al3 Ti composite

Study on Ti Fiber Reinforced Tial3 Composite by Infiltration-In Situ Reaction

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

In situ Al-TiB composite obtained by stir casting

Synthesis of C F /tial 3 Composite by Infiltration-In Situ Reaction

Preparation and characteristics of Ti3AlC2 -Al3Ti/Al composite materials synthesized from pure Al and Ti3AlC2 powders

Processing of in situ aluminum-matrix composites and controlling of the solidification microstructures

Preparation of ti-al based nanophase composite powder by mechanical alloying

Evaluation of the microstructure of in-situ reaction processed Al3Ti-Al2O3-Al composite

In Situ Synthesis and Properties of Ti<sub>3</sub>AlC<sub>2</sub>/TiB<sub>2</sub> Composites

In Situ Fabrication and Properties of (Al3Ti)P/6351 Composites

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents

Strengthening Ti3AlC2 by in Situ Synthesizing Ti3AlC2–Y4Al2O9 Composites

Revealing the formation, strengthening and toughening mechanism of a new (Ti3AlC2+Al2O3)p /Al3Ti composite with strength-ductility synergy

Ti3alc2-Al2o3-Tial3 Composite Fabricated by Reactive Melt Infiltration

In Situ Fabrication of (tib+al_2o_3)/ti Matrix Composites

Microstructure and property of Al/TiC composites prepared by reaction synthesis

Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder