Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Study of sintering behavior and dielectric properties of phosphor-doped barium titanate

Effect of Phosphor Doping on the Microstructure and Dielectric Properties of Barium Titanate Ceramics

The Effect of B2o3-Li2co3 Addition on Sintering Behavior and Dielectric Properties of Ba0.6sr0.4tio3 Ceramics

Effect of sintering process on dielectric properties of B2O3-doped Ba1-xSrxTiO3 graded ceramics

Effects of Sintering Temperature and Bi2O3, Y2O3 and MgO Co-Doping on the Dielectric Properties of X8R BaTiO3-based Ceramics

Dopant behaviours of Sm2O3 on microstructure and properties of barium zirconium titanate ceramics

Effect of sintering process on dielectric properties of B2O3-doped graded ceramics

Effect of Dy2O3-Doping on Microstructure and Properties of BaTiO3 Ceramic

Dopant Behaviours of Sm_2O_3 on Microstructure and Properties of Barium Zirconium Titanate Ceramics

The Effect of Different Doping Methods of Sintering Aids on the Barium Titanate Based X7R Ceramics

Yttrium Doping Behavior in BaTiO3 Ceramics at Different Sintered Temperature

Effect of sintering atmospheres on the microstructure and dielectric properties of Yb/Mg co-doped BaTiO3 ceramics

Study Of Temperature-Stable Batio3 Dielectric Ceramics Modified With Bi2o3 And Rare-Earth Oxides

Study of Physicochemical and Optical Characteristics of Doped Barium Titanate Ceramics Materials for Optoelectronic Devices

INFLUENCE OF RARE-EARTH DOPING ON MICROSTRUCTURE AND DIELECTRIC PROPERTIES OF BARIUM TITANATE CERAMICS SINTERED IN REDUCING ATMOSPHERE

EFFECT OF DOPING CaO ON DIELECTRIC PROPERTIES OF BaZr0.05Ti0.95O3 CERAMICS

Effect of Pr3+ doping concentration on microstructure and optical properties of transparent BaF2 ceramics

Effect of sintering temperature on microstructure, dielectric and ferroelectric properties of BaTiO3 ceramics

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Influence of BaPbO3 doping on properties of (Sr, Pb) TiO3 ceramics

The effect of doping process on microstructure and dielectric properties of BaTiO 3 -based X7R materials