Abstract:In the past few years,ceramic laser materials have emerged with many advantages,such as lower cost fabrication,high melting temperature and large size samples more easily to be manufactured,as compared to crystals and glasses.There has been remarkable interest in rare-earth-doped ferroelectric ceramics which are suitable material for novel integrated-optic devices formed by a combination of lasers/amplifier with electro-optic(EO)and nonlinear-optic waveguide components.Recently,a new highly transparent,electro-optic ceramic material,Er3+ and Er3+/Yb3+ ions doped Pb1-xLaxZryTi1-yO3(PLZT),have been fabricated,which have exceptionally high electro-optic(EO)effect.The up-conversion luminescence of Er3+ and Er3+/Yb3+ ions doped PLZT for active electro-optical applications has been investigated.The green light of 540 nm and 566 nm can be observed in Er3+ doped PLZT.Moreover,their intensity gets stronger along with concentration of Er3+.In Er3+/Yb3+ co-doped PLZT,besides the green light of 540 nm and 566 nm,a relatively weak red light of 668 nm can also be observed.To all sample,the nonlinear curves fitting to the relationship between up-conversion intensity and excitation intensity were made,which were concluded that both red emission and green emission were the absorption process of double-photon.And again the character of up-conversion luminescence was discussed using the Raman spectra of PLZT.The theory and experimentation both show Er3+ and Er3+/Yb3+ ions doped PLZT,based on its large electro-optical effect,have a prospect to be applied for electro-optic Q-switched double-function up-conversion laser device.

Upconversion luminescence from Er3+ doped ZnS pumped by a 960nm laser diode

The upconversion luminescence of Er in noncrystal ZBLAN

Luminescence of Er Doped ZnS Quantum Dots Excited by Infrared Lasers.

Luminescence Spectroscopy and Visible Upconversion Properties of Er3+ in Zno Nanocrystals

Up-conversion characteristics of Er3+/Yb3+ co-doped heavy mental fluoride glass

Upconversion luminescence of single-crystalline ZnO by femtosecond laser irradiation

Studies on Upconversion Mechanism of ZrO2 ： Er^3＋, Yb^3＋ Nanocrystals under Excitation at 488 and 980 Nm

Highly Efficient Saturated Visible Up-Conversion Photoluminescent Y2o3:Er3+ Microspheres Pumped With A 1.55 Mu M Laser Diode

Enhanced Green Up-Conversion Luminescence in In2O3:Yb3+/Er3+ by Tri-Doping Zn2+

Fabrication and Luminescene Properties of ZnS: Er Quantum Dots Material Pumped by 980 Nm LD

Infrared-to-visible Upconversion Luminescence of Er3+ and Yb3+ Co-Doped Germanate Glass

Upconversion properties and mechanisms in Er<sup>3</sup>+ ions upon 800 nm excitation

Up-conversion Luminescence of Er~(3+)and Er~(3+)/Yb~(3+)Ions Doped PLZT for Active Electro-optical Applications

[The Upconversion "characteristic Saturation Phenomenon" of ErYb:ZBLAN Glass Excited by 966 Nm Diode Laser].

High Efficiency Infrared to Visible Upconversion in Er3+/Yb3+-Doped Lead Halide Tellurite Glass

Orange-red upconversion luminescence of Sm[sup 3+]-doped ZnO-B[sub 2]O[sub 3]-SiO[sub 2] glass by infrared femtosecond laser irradiation

Upconversion properties of the Er3+ doped 20GaF3–15InF3–20CdF2–15ZnF2–20PbF2–10SnF2 glasses

Mechanistic Investigation of Upconversion Luminescence in Er3+-doped BaCl2, BaF2 and NaYF4 Phosphors

Up-conversion luminescence of Y2O3: Yb, Er under 1.55 μm excitation

Up-conversion luminescence properties of Li+ and rare earth ions co-doped ZrO2 nanocrystalline powders

Upconversion Properties Of The Er 3(+) Doped 20gaf(3)-15inf(3)-20cdf(2)-15znf(2)-20pbf(2)-10snf(2) Glasses