Abstract:The effect of annealing on the upconversion luminescence of ZnO:Er3+ nanocrystals was investigated in detail. The green and the red upconverted emissions under infrared 978-nm light excitation were remarkably enhanced with an increase of annealing temperature. Moreover, for the sample annealed at 500 degrees C, the ratio of the intensity of H-2(11/2) -> I-4(15/2) emission to that of S-4(3/2) -> I-4(15/2) emission increased from less than to more than unity with an increase of the excitation density. However, the same case did not occur to the sample annealed at 700 degrees C, where the ratio was independent of excitation density except when the excitation density was higher than 42 700 W/cm(2). This distinction was attributed mainly to the difference in energy gap between the H-2(11/2) and S-4(3/2) states in the two samples, originating from the local microstructure variation around Er3+ ions. In addition, a high thermal sensitivity of 0.0062/degrees C was obtained in the ZnO:Er3+ nanocrystals based on the temperature-dependent fluorescence intensity ratio (FIR) of the green upconverted emission, which would make this material a promising candidate for the nanoscaled thermal sensor of high accuracy and resolution.

Luminescence Spectroscopy and Visible Upconversion Properties of Er3+ in Zno Nanocrystals

Enhanced Upconverted Photoluminescence in Er3+ and Yb3+ Codoped ZnO Nanocrystals with and Without Li+ Ions

Up-conversion luminescence properties of Li+ and rare earth ions co-doped ZrO2 nanocrystalline powders

Efficient two-color luminescence of Er3+/Yb3+/Li +:ZrO2 nanocrystals

Effect Of Annealing On Upconversion Luminescence Of Zno : Er3+ Nanocrystals And High Thermal Sensitivity

Upconversion photoluminescence of ZrO2:Er3+ nanocrystals synthesized by using butadinol as high boiling point solvent

Enhancement of the Upconversion Photoluminescence Intensity in Li+ and Er3+ Codoped Y2o3 Nanocrystals

Luminescence Spectroscopy and Near-Infrared to Visible Upconversion in Er3+ and Yb3+ Codoped Sc2O3 Nanoparticles

The Effect Of Li On The Spectrum Of Er(3+) In Li- And Er-Codoped Zno Nanocrystals

Er3+- Doped ZnO Nanospheres with Enhanced Upconversion Photoluminescence Produced Through Sonochemical Synthesis

Local Electronic Structure and Luminescence Properties of Er Doped ZnO Nanowires

Single Band Upconversion Mechanisms Of Er3+/Yb3+:Zro2 Nanocrystals

Effect of Zn2+ Ions on Upconversion Emission of Er3+ in Zn/Er:Linbo3 Crystal

Enhancement of Upconversion Luminescence of Y2O3:Er3+ Nanocrystals by Codoping Li+–Zn2+

Up-conversion Luminescence of Trivalent Erbium Ions Doped Zirconia Nanocrystalline

Studies on Upconversion Mechanism of ZrO2 ： Er^3＋, Yb^3＋ Nanocrystals under Excitation at 488 and 980 Nm

Upconversion luminescence properties of Li<sup>+</sup>-doped ZnWO<sub>4</sub>:Yb,Er

Enhanced red upconversion emission of Er3+-doped ZnO by post-annealing

Spectral performance and intensive green upconversion luminescence in Er3+/Yb3+-codoped NaY(WO4)2 crystal

Up-conversion Luminescence Property of Er~(3+) Ions Doped Nanocrystalline Yttrium Oxide

Structure and up-conversion luminescence properties in Er3+-doped TiO2 nanocrystals