Abstract:A novel method was developed to polymerize acrylamide in an opaque inverse emulsion system by UV light initiation, which was usually used in a transparent system or semi-transparent system, such as solution systems and micro-emulsion systems. Using 2,2-Dimethoxy-2-phenylacetophenone (DMPA) as an initiator, Span80 + OP10 as a blend emulsifier,the inverse emulsion polymerization of acrylamide in kerosene could be completed in about 20 min with exposure under a medium pressure mercury lamp and proper mixing, and the molecular weight of the produced polymer was as high as 10(7). No constant polymerization rate period was observed throughout the whole polymerization process, and there was no dramatic difference between the size of the initial monomer droplets and the size of the final inverse latexes according to scanning electron microscope observation, indicating that the polymerization was nucleated inside the monomer droplets. The influences of the type and concentration of photoinitiator, monomer concentration, emulsifier percentage and reaction temperature on polymerization were investigated. The initiating activity of photoinitiators is in an order of Irgacure 2959 > (ITX + EDAB) > BDK. When the concentration of photoinitiator increases, the reaction rate increases at first, then begins to decrease after the reaction rate reaches a maximum value. Both the reaction rate and the molecular weight increase when the monomer concentration increases. With the increase of the emulsifier percent age the reaction rate increases I while no dramatic change displays in the molecular weight. The overall activation energy of polymerization was measured as 13.34 kJ/mol.

Inverse suspension polymerization of sodium acrylate

Inverse Suspension Polymerization of Polyacrylate Sodium

Synthesis of Poly(N-isopropylacrylamide) Hydrogel Particles

Stability Study of Inverse Suspension Copolymerization of 1,1,3,3‐tetramethylguandium Acrylate and N,N′‐methylenebisacrylamide

Photoinitiated Inverse Emulsion Polymerization of Sodium Acrylate

Kinetic Analysis of the<sup>60</sup>Co γ Ray-Initiated Inverse Emulsion Polymerization of Sodium Acrylate Solutions

Investigation on the Inverse Emulsion Polymerization of Acrylic Acid

Radiation Copolymerization of Acrylamide and Cationic Monomer in an Inverse Emulsion

Kinetics of the Potassium Persulfate-Initiated Inverse Emulsion Polymerization of Sodium Acrylate Solutions

Kinetic model for the 60Co-γ ray initiated inverse emulsion polymerization of sodium acrylate solutions

Ampholytic Terpolymers of Acrylamide with Sodium Acrylate and (2-Methacryloyloxyethyl)trimethylammonium Chloride. Synthesis with 60co Γ-Ray and Polymerization Kinetics

Kinetic-Model For The Co-60-Gamma Ray Initiated Inverse Emulsion Polymerization Of Sodium Acrylate Solutions

Studies of inverse emulsion copolymerization of (2-methacryloyloxyethyl) trimethyl ammonium chloride and acrylamide

Inverse Emulsion Polymerization of Acrylamide Initiated by Uv Radiation

Effects Of Water Solubility Of Acrylonitrile On Vinylidene Chloride/Acrylonitrile/Styrene Suspension Polymerization

Ab Initio RAFT Emulsion Copolymerization of Styrene and Acrylonitrile

Synthesis of poly( acrylic acid) nano- and microparticles using an inverse emulsion polymerization method

Kinetics of Emulsion Copolymerization of (2-Methacryloyloxyethyl) Trimethyl Ammonium Chloride and Acrylamide with Gamma Rays

Applied Research of Polymerizable Emulsifier in Acrylic Emulsion Polymerization

STUDY ON THE FORMATION MECHANISM OF MONODISPERSE PARTICLES IN THE EMULSIFIER-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Polymerization Of Butyl Acrylate In Anionic Microemulsion